Tendo em vista o importante papel desempenhado pelos selantes de fossas e fissuras na prevenção da cárie dental, o objetivo do presente estudo foi avaliar in vitro propriedades mecânicas, químicas e ntimicrobianas do selante isento de bisfenol A Embrace Wetbond™. Para os testes de resistência ao cisalhamento e microinfiltração foram selecionados 135 terceiros molares hígidos, extraídos de humanos, divididos aleatoriamente em 6 grupos: (I) selante Fluroshield® sem contaminação; (II) selante Embrace Wetbond™ sem contaminação; (III) selante Fluroshield® contaminado com saliva; (IV) selante Embrace Wetbond™ contaminado com saliva; (V) selante Fluroshield® contaminado com água; e (VI) selante Embrace Wetbond™ contaminado com água. No estudo de resistência ao cisalhamento os dentes foram seccionados no sentido vestíbulo-lingual, a porção radicular removida e as superfícies mesiais e distais foram embebidas em resina de poliéster. Após o condicionamento do esmalte, foi aplicado o selante com o auxílio de uma matriz de Teflon®. Os espécimes foram termociclados e submetidos ao teste de resistência ao cisalhamento com uma velocidade de 0,5mm/min e célula de carga de 50kgf. Os resultados foram comparados empregando a análise de variância (ANOVA) e pós-teste de Tukey. No estudo de microinfiltração, após o condicionamento do esmalte foi aplicado o selante. Os dentes foram termociclados, selados na região da câmara pulpar com resina composta, isolados, imersos em solução de rodamina B a 0,2%, incluídos em resina acrílica, seccionados, lixados, montados em lâminas, identificados e analisados em microscópio óptico para quantificação da microinfiltração. Os resultados foram comparados empregando o teste de Kruskal-Wallis e o pós-teste de Dunn. No estudo de liberação de fluoreto por meio de água aquecida e saliva artificial foram selecionados dois selantes resinosos contendo fluoreto (Embrace Wetbond™ e Fluroshield®), uma resina composta micro-híbrida (FiltekTM Z-250) e um cimento de ionômero de vidro (Vidrion R). As determinações de fluoreto foram realizadas por potenciometria direta, utilizando o eletrodo seletivo combinado de fluoreto. Para o teste de liberação de fluoreto em saliva artificial foram confeccionados 8 corpos de prova de cada material , os quais foram armazenados em tubos plásticos contendo saliva artificial, substituída diariamente. Após 15 dias, foi avaliada a quantidade de fluoreto liberado nas soluções. Os valores obtidos em mV foram convertidos em ppm (μg/ml). Os resultados foram comparados empregando a análise de variância (ANOVA) e o pós-teste de Tukey. No estudo da atividade antimicrobiana, efetuado por meio do teste de difusão em ágar pelo método do poço, foram selecionados dois selantes resinosos contendo fluoreto (Embrace Wetbond™ e Fluroshield®), um cimento de ionômero de vidro (Vidrion R), solução de digluconato de clorexidina a 1% e soro fisiológico. Foram utilizadas cepas de S. mutans (ATCC 25175 e cepa de campo), na densidade de 1-2 da escala de McFarland. Após o período de incubação, a zona de inibição do crescimento microbiano foi mensurada. Os resultados foram comparados empregando a análise de variância ANOVA e o pós-teste de Bonferroni. O nível de significância em todas as análises estatísticas foi de 5%. No estudo da dosagem de bisfenol A foram selecionados dois selantes resinosos (Embrace Wetbond™ e Fluroshield®), dispensados em recipientes contendo 3ml de metanol. Após homogeneização e filtragem, os extratos foram analisados utilizando um espectrômetro de massas por cromatografia gasosa. Foram realizados testes com as fórmulas moleculares do bisfenol A (C15H16O2) e do Bis-GMA (C29H36O8). Com base nos resultados obtidos pôde-se concluir que o selante Embrace Wetbond™ apresentou resistência ao cisalhamento próxima do mínimo aceitável e alta microinfiltração, quando utilizado de acordo com as indicações do fabricante, em condições de contaminação com umidade. Por outro lado, esse selante apresentou elevada liberação de fluoreto, tanto em água aquecida quanto em saliva artificial, apresentou elevada atividade antimicrobiana e não apresentou liberação de bisfenol A e de Bis- GMA. / Considering the important role of pit-and-fissure sealants on the prevention of dental caries, the purpose of this study was to evaluate in vitro the mechanical, chemical and antimicrobial properties of the bisphenol A-free pit-and-fissure sealant Embrace Wetbond™. For the shear bond strength and microleakage tests, 135 sound human third molars were selected and randomly assigned to 6 groups: (I) Fluroshield® sealant without contamination; (II) sealant Embrace Wetbond™ without contamination; (III) Fluroshield® sealant contaminated with saliva; (IV) Embrace Wetbond™ sealant contaminated with saliva; (V) Fluroshield® sealant contaminated with water; and (VI) Embrace Wetbond™ sealant contaminated with water. For the shear bond strength test, the teeth were sectioned in a buccolingual direction, the root portion was removed and the mesial and distal surfaces were embedded in polyester resin. The sealant was applied to the acid-etched enamel with the aid of Teflon® matrix. The specimens were thermocycled and subjected to a shearing force at a crosshead speed of 0.5mm/min with a 50kgf load cell. Data were analyzed statistically by analysis of variance (ANOVA) and Tukeys post-test. For the microleakage assay, after acid etching of enamel, the teeth were thermocycled, the pulp chamber was sealed with composite resin, and the teeth were rendered waterproof, immersed in 0.2% B rhodamine solution, embedded in acrylic resin, sectioned, ground, mounted on glass slides, identified and analyzed with an optical microscope for quantification of microleakage. The results were compared by the Kruskal-Wallis and Dunns post-test. Two fluoride-containing resin sealants (Embrace Wetbond™ and Fluroshield®), a microhybrid composite resin (FiltekTM Z-250) and a glass ionomer cement (Vidrion R) were selected for the fluoride release test in heated water and artificial saliva. Fluoride measurements were performed with a direct potentiometry using a fluoride ion selective electrode. For the test in saliva artificial, 8 specimens of each material were fabricated and stored in plastic tubes containing artificial saliva, which as daily renewed. The amount of fluoride released in the solutions after 15 days was analyzed, and the the values obtained in mV were converted into PPM (μg/mL). The results were compared by ANOVA and Tukeys post-test. Two fluoride-containing resin sealants (Embrace Wetbond™ and Fluroshield®), a glass ionomer cement (Vidrion R), 1% chlorhexidine digluconate solution and saline were selected for the analysis of the antimicrobial activity using the agar-well diffusion assay. Suspensions of S. mutans strains (ATCC 25175 and field strain) with density equivalent to the 1-2 McFarland scale were used. After incubation, the zones of microbial growth inhibition were measured. The results were compared by ANOVA and Bonferroni post-test. A significance level of 5% was set for all statistical analyses. For the analysis of bisphenol A dosage, two resin sealants (Embrace Wetbond™ and Fluroshield®) were delivered in receptacles containing 3ml of methanol. After homogenization and filtering, the extracts were analyzed under gas chromatography-mass spectroscopy and tests were performed with the molecular formulas of bisphenol A (C15H16O2) and Bis-GMA (C29H36O8). Based on the obtained results, it may be concluded that the sealant Embrace Wetbond™ presented shear bond strength near of the minimum acceptable and great microleakage when used according to the manufacturers instructions under moisture contamination conditions. On the other hand, this sealant presented high fluoride release in both heated water and artificial saliva, showed high activity antimicrobial and did not present release of bisphenol A or Bis-GMA.
| Identifer | oai:union.ndltd.org:IBICT/oai:teses.usp.br:tde-30082010-082800 |
| Date | 21 May 2010 |
| Creators | Soraia Monique Fiorati Aguiar |
| Contributors | Paulo Nelson Filho, Maria Cristina Borsatto, Silmara Aparecida Milori Corona, Jose Carlos Pettorossi Imparato, Sizenando de Toledo Porto Neto |
| Publisher | Universidade de São Paulo, Odontopediatria, USP, BR |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da USP, instname:Universidade de São Paulo, instacron:USP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.003 seconds