Indiana University-Purdue University Indianapolis (IUPUI) / The objective of this study was to evaluate the in vivo performance of the novel
press-fit dental implant fabricated via electron beam melting (EBM, Southern Methodist
Univ.) and compare it to a commercially-available porous-coated press-fit dental implant
(Endopore, Innova Corp.).
Twelve cylindrical shaped implants 3 mm in diameter x 5 mm long were made by
EBM (Southern Methodist Univ.) using Ti6Al4V ELI alloy. Twelve commercial
implants (Endopore, Innova Corp.) of the same geometry were used as controls. Samples
were implanted in rabbit tibia and retrieved six weeks postoperatively. Six specimens from each implant type were embedded undecalcified, sectioned, and stained with
toluidine blue (Sigma) for histomorphometry analysis. Bone-to-implant contact (BIC)
was measured. On the six remaining samples from each implant type, the mechanical
properties were evaluated by pushout test on a material testing machine. The samples
were loaded at a loading rate of 1 mm/min. The pushout strength was measured and the
apparent shear stiffness was calculated. The results were analyzed with a paired-t test.
The histology shows osteointegration of surrounding bone with both implant
types. Bone was found to grow into the porous space between the beads. Both the
Endopore (Innova Corp.) and the EBM (Southern Methodist Univ.) showed similar BIC.
The mean BIC for the Endopore (Innova Corp.) and EBM (Southern Methodist Univ.)
implant were 35 ± 6% and 32 ± 9%, respectively. It failed to reach statistical significance
(p > 0.05). The peak pushout force for Endopore (Innova Corp.) and EBM (Southern
Methodist Univ.) implants were 198.80 ± 61.29 N and 243.21 ± 69.75 N, respectively.
The apparent shear stiffness between bone and implant for the Endopore (Innova Corp.)
and EBM (Southern Methodist Univ.) implants were 577.36 ± 129.99 N/mm; and 584.48
± 146.63 N/mm, respectively. Neither the peak pushout force nor the apparent shear
stiffness of the implants was statistically different between the two groups (p > 0.05).
The results suggest that the implants manufactured by EBM (Southern Methodist Univ.)
perform equally well as the commercial implant Endopore (Innova Corp.) in this current
animal model.
Identifer | oai:union.ndltd.org:IUPUI/oai:scholarworks.iupui.edu:1805/2224 |
Date | January 2010 |
Creators | Khouja, Naseeba, 1981- |
Contributors | Chu, Tien-Min Gabriel, Brown, David T., Platt, Jeffery A., 1958-, Blanchard, Steven B., Levon, John A. |