Previous issue date: 2008 / Fundação Oswaldo Cruz. Centro de Pesquisas Gonçalo Moniz. Salvador, Bahia, Brasil / 0 objetivo deste trabalho foi avaliar histomorfometricamente, por microscopia de luz comum, o potencial osteogênico de matrizes colagênicas aniônicas, reticuladas ou não em glutaraldeído, implantadas em defeitos ósseos críticos, em calvária de ratos. Foram utilizados 86 ratos divididos aleatoriamente para compor quatro grupos: Gl - matriz colagênica aniônica com 24h de hidrólise e 15min de reticulação em GA 0,05% (MCAHGA); Gll - matriz colagênica aniônica com 24h de hidrólise (MCA); GUI - matriz colagênica neutra, controle positivo (MCN) e GIV - defeito ósseo vazio, sem implantação de biomaterial, preenchido por coágulo sanguíneo, controle negativo. Os animais foram avaliados nos pontos biológicos de 15, 45, 90 e 120 dias. Os resultados evidenciaram que os biomateriais implantados nos grupos I e II foram biocompatíveis, embora tenham desencadeado inflamação crônica granulomatosa discreta e regressiva. Estas matrizes apresentaram velocidade de biodegradação compatível com a neoformação óssea, a qual se mostrou associada a angiogênese no interior das matrizes, em todos os pontos biológicos. No GUI, a fragmentação e biodegradação mostraram-se acentuadas, pela ausência de tratamento químico do colágeno. A neomineralização evidenciada nos grupos I e II apresentou aumento estatisticamente significante ao longo dos tempos. O percentual de mineralização do Gll (87%) foi estatisticamente diferente daquele encontrado no Gl (66%). Ao compararmos estes percentuais com a mineralização observada no GIV, notam-se diferenças muito significantes. Neste último, assim como no GUI, a neoformação óssea esteve limitada às bordas do defeito com fibrose na área seccional do defeito. Conclui-se que as matrizes colagênicas aniônicas apresentaram potencial osteogênico mais evidente nas matrizes sem reticulação em glutaraldeído. Estas matrizes apresentam grande potencial de aplicabilidade clínica, nas terapias regenerativas ósseas / The aim of this study was to make a histomorphometric evaluation by common light microscopy, of the osteogenic potential of anionic collagen matrices, either reticulated in glutaraldehyde or not, implanted in critical bone defects in rat calvarias. In this study 86 rats were used, randomly divided into four groups: Gl - anionic collagenous matrix with 24h of hydrolysis and 5 min of reticulation in GA 0.05% (MCAHGA); Gll - anionic collagenous matrix with 24h of hydrolysis (MCA); Gill - neutral collagenous matrix, positive control (MCN) and GIV - empty bone defect, without biomaterial implantation, filled with blood coagulum, negative control. The animals were evaluated at the biological points of 15, 45, 90 and 120 days. The results evidenced that the biomateriais implanted in groups I and II were biocompatible, although they had set of chronic, discrete and regressive granulomatous inflammation. These matrices presented a speed of biodégradation compatible with bone neoformation, which was shown to be associated with angiogenesis inside the matrices at all the biological points. In G III, fragmentation and biodégradation were shown to be accentuated by the absence of chemical treatment of the collagen. The neomineralization evidenced in Groups I and II presented statistically significant increase throughout the times. The percentage of mineralization of Gll (87%) differed statistically from that found in Gl (66%). When these percentages were compared with the mineralization observed in GIV, very significant differences were noted. In the latter, as in Gill, bone neoformation was limited to the edges of the defect with fibrosis in the sectional area of the defect. It was concluded that the anionic collagen matrices presented more evident osteogenic potential in the matrices without reticulation in glutaraldehyde. These matrices presented a great potential for clinical application in bone regenerative therapies.
Identifer | oai:union.ndltd.org:IBICT/oai:www.arca.fiocruz.br:icict/5890 |
Date | January 2008 |
Creators | Miguel, Fúlvio Borges |
Contributors | Freitas, Luiz Antonio Rodrigues de, Granjeiro, José Mauro, Rossi, Alexandre Malta, Santos, Washington Luis Conrado dos, Araújo, Iguaracyra Barreto de Oliveira, Rosa, Fabiana Paim |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Source | reponame:Repositório Institucional da FIOCRUZ, instname:Fundação Oswaldo Cruz, instacron:FIOCRUZ |
Rights | Fúlvio Borges Miguel, info:eu-repo/semantics/openAccess |
Page generated in 0.0027 seconds