Submitted by Renata Lopes (renatasil82@gmail.com) on 2017-12-08T17:00:54Z
No. of bitstreams: 1
felixsoaresdelimaneto.pdf: 3304649 bytes, checksum: 1cb4641ba963788c0c4b2143b23a8c5d (MD5) / Approved for entry into archive by Adriana Oliveira (adriana.oliveira@ufjf.edu.br) on 2017-12-22T11:34:06Z (GMT) No. of bitstreams: 1
felixsoaresdelimaneto.pdf: 3304649 bytes, checksum: 1cb4641ba963788c0c4b2143b23a8c5d (MD5) / Made available in DSpace on 2017-12-22T11:34:06Z (GMT). No. of bitstreams: 1
felixsoaresdelimaneto.pdf: 3304649 bytes, checksum: 1cb4641ba963788c0c4b2143b23a8c5d (MD5)
Previous issue date: 2011-11-28 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Neste trabalho foram estudados vidros borossilicatos dopados com nanopartículas de enxofre
e íons de Er+3 com o objetivo de determinar a difusividade térmica do sistema
vítreo (SNABP), através da técnica de Espectroscopia de Lente Térmica. As propriedades
espectroscópicas de tais amostras foram investigadas por meio das medidas de absorção
_óptica na região espectral de 400 a 2000 nm. A caracterização das propriedades termo-
_ópticas foram realizadas por meio da espectroscopia de Lente Térmica de feixe duplo no
modo descasado com excitação em 50mW a 3W. Verificou-se que a difusividade térmica
diminuiu quando a matriz SNABP foi dopada com nanocristais de PbS e íons Er3+. Com
o tratamento térmico, a amostra SNABP Er manteve a menor difusividade praticamente
em todos os tempos. Os resultados foram discutidos em termos de transporte de calor
por fônons, onde a redução da difusividade térmica observada foi analisada considerando
a diminuição do livre caminho médio dos fônons devido aos efeitos de espalhamento. / In this work we studied borosilicate glasses doped with nanoparticles of sulfur and Er3+
ions in order to determine the thermal diffusivity of the glassy system (SNABP), using the
thermal lens technique. The spectroscopic properties of these samples were investigated
by measuring absorption in the optical spectral region from 400 to 2000nm. The characterization
of the thermo-optic properties was performed by thermal lens tecniqueby with
excitation at 50mW to 3W. It was found that the thermal difusivity decreased when the
SNABP matrix was doped with PbS nanocrystals and Er3+ ions. Thermal treatment of
the SNABP samples reduced the thermal difusivity. The results were discussed in terms
of heat transport by phonons, where the observed reduction in thermal diffusivity was
analyzed considering the decrease in the mean free path of phonons due to the scattering
effects.
Identifer | oai:union.ndltd.org:IBICT/oai:hermes.cpd.ufjf.br:ufjf/6006 |
Date | 28 November 2011 |
Creators | Lima Neto, Felix Soares de |
Contributors | Bell, Maria José Valenzuela, Dantas, Noelio Oliveira, Dias, Rodrigo Alves |
Publisher | Universidade Federal de Juiz de Fora (UFJF), Programa de Pós-graduação em Física, UFJF, Brasil, ICE – Instituto de Ciências Exatas |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Repositório Institucional da UFJF, instname:Universidade Federal de Juiz de Fora, instacron:UFJF |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0024 seconds