Eletrofiação de fibras de borracha natural com adição de polianilina /

Orientador: Aldo Eloizo Job / Co-orientador: Deuber Lincon da Silva Agostini / Banca: Claudia Merlini / Banca: Neri Alves / O Programa de Pós Graduação em Ciência e Tecnologia de Materiais, PosMat, tem caráter institucional e integra as atividades de pesquisa em materiais de diversos campi / Resumo: A técnica de eletrofiação tem sido utilizada na obtenção de fibras com diversos materiais poliméricos. Neste trabalho, foram desenvolvidos, de maneira inédita, materiais eletrofiados a partir de borracha natural e polianilina. Por esta técnica, foram obtidas mantas eletrofiadas com fibras de diâmetro menor que 1 um. Para o desenvolvimento destas mantas eletrofiadas tornou-se necessário primeiramente realizar um amplo estudo sobre os parâmetros de processo, o qual constou em variar o fluxo de vazão da solução polimérica de 0.1, 0,25, 0,5 mL/h, a tensão aplicada ao processo de 10, 12,5....., 15 kV e a rotação do coletor rotativo onde as fibras foram depositadas em 30, 40, 50 rpm. Após o estudo dos parâmetros de eletrofiação, foi selecionada uma série com os melhores parâmetros, que proporcionou a obtenção de mantas de borracha natural denominada BN. Estas mantas foram posteriormente recobertas com polianilina pelo método de polimerização in situ, obtendo mantas de BN/PAni dopada e BN/PAni desdopada. Para fins de comparação foram também produzidas membranas densas pelo método casting, que foram caracterizadas quanto suas propriedades elétricas, onde mostrou bons resultados, se comportando como material ôhmico alcançando a condutividade na ordem de 10-6 S/m para BN/PAni dopada, enquadrado assim entre os materiais semicondutores. Além das propriedades elétricas foram também investigadas as propriedades térmicas, espectroscópicas dos materiais estudados. Os resultados deste trabalho mostraram que é possível eletrofiar a borracha natural formando fibras de diâmetro que alcançaram valores mínimos de até 0,92 um / Abstract: The electrospinning technique has been used to obtain fibers with various polymer materials. In this work were developed in an unprecedented fibers electrospun from natural rubber and polyaniline. For this technique, fibers mats were obtained with fiber diameter of less than 1 micrometers. For the development of these electrospun mats became necessary to first perform an extensive study on the process parameters, which consisted in varying the flow of polymer solution at 0.1, 0.25, 0.5 ml/h, the voltage applied to the process 10, 12.5, 15 kV and rotation of the collector where the fibers were deposited on 30, 40, 50 rpm. After studying the electrospinning parameters, it selected a series with the best parameters, which provided obtaining natural rubber mats called NR. These mats were covered with polyaniline by in situ polymerization method, getting NR/PAni doped and NR/PAni undoped mats. For purposes of comparison were also produced membranes by casting method, which were characterized as its electrical properties, which showed good results, behaving as ohmic materials reaching the conductivity on the order of 10-6 S/m for NR/PAni doped, entering among the semiconductor materials. In addition to the electrical properties were also investigated the thermal, spectroscopic and morphological materials properties. These results showed that it is possible produced natural rubber fibers electrospun forming diameter fibers that have reached minimum values of up to 0.92 micrometers / Mestre

Identiferoai:union.ndltd.org:UNESP/oai:www.athena.biblioteca.unesp.br:UEP01-000864825
Date January 2016
CreatorsDognani, Guilherme.
ContributorsUniversidade Estadual Paulista "Júlio de Mesquita Filho" Faculdade de Ciências e Tecnologia.
PublisherPresidente Prudente,
Source SetsUniversidade Estadual Paulista
LanguagePortuguese, Portuguese, Texto em português; resumo em inglês
Detected LanguageEnglish
Typetext
Format78 f. :
RelationSistema requerido: Adobe Acrobat Reader

Page generated in 0.0022 seconds