Environmental stress cracking (ESC) is a significant problem that has plagued the plastics industry since its discovery nearly 70 years ago. The accelerated brittle failure brought about when a stressed polymer comes in contact with an aggressive environment can happen suddenly with destructive results. Many classes of polymers are susceptible to this type of slow crack growth; however special emphasis has typically been placed on polyolefins due to their wide range of working environments, market dominance and their seemingly chemical resistance. Much research has been focused on formulating environmentally resistant materials, while the evaluation techniques for gauging environmental stress cracking resistance (ESCR) seem to have been left behind. This research focuses on developing a reliable testing technique for evaluating the ESCR of polyethylene resins.
Passive acoustic monitoring was adapted to an industrially accepted ESCR test in an attempt to hear polymer damage before it was visually apparent. It was discovered that the low energy released during the early stages of damage and excessive background noise masked passive signals, making this method of evaluation impractical. Alternatively, active ultrasonic monitoring through velocity and attenuation measurements was investigated to see if probing techniques could be used to detect structural damage. Active ultrasonic monitoring of static and tensile stressed samples were able to differentiate plasticization after ageing, however no indication of ESCR properties could be inferred.
A novel forced based monitoring system was developed in response to the acoustic testing techniques. Force monitoring was able to provide useful information regarding the failure cycle of ESC and the acquired profiles could describe a failure onset time. Several ageing environments were also tested with force monitoring and a traditional ESCR test to reveal the stress cracking ability of biodiesel, an important finding. / Thesis / Master of Applied Science (MASc) / Accelerated failure of stressed plastics can occur upon exposure to fluids through a phenomenon known as environmental stress cracking (ESC). The following research outlines the development of a novel testing technique to gauge a material’s environmental stress cracking resistance (ESCR). Adaption of passive acoustics to an existing stress cracking test was unable to provide any indication of ESCR, however the use of active ultrasonics was able to show sample plasticization. A novel forced based measuring technique was found to uniquely map the failure progression of a sample undergoing ESC, providing valuable information for understanding the phenomenon. Additional testing was also completed on various environmental fluids to reveal biodiesel’s ability to provoke ESC, an important observation.
| Identifer | oai:union.ndltd.org:mcmaster.ca/oai:macsphere.mcmaster.ca:11375/21660 |
| Date | January 2017 |
| Creators | West, William T.J. |
| Contributors | Thompson, Michael, Chemical Engineering |
| Source Sets | McMaster University |
| Language | English |
| Detected Language | English |
| Type | Thesis |
Page generated in 0.002 seconds