Orientador : Cinthia Pereira Machado Tabchoury / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-31T20:29:53Z (GMT). No. of bitstreams: 1
Dalcico_Roberta_M.pdf: 7072824 bytes, checksum: a5b81080124c085a4e07e2df27d050bd (MD5)
Previous issue date: 2002 / Resumo: Vários trabalhos in vitro e in vivo mostram que os cimentos de ionômero de vidro (CIVs) são capazes de diminuir cáries recorrentes. Além disso, alguns estudos têm sugerido que esses materiais podem apresentar efeito inibitório sobre a microbiota cariogênica. Tal efeito tem sido atribuído a alguns componentes liberados pelo material, entre eles flúor (F) e alumínio (AI). Desta maneira, o objetivo deste estudo foi analisar bioquímica e microbiologicamente a placa formada sobre dois cimentos de ionômero de vidro, bem como avaliar os efeitos da liberação de F e AI na proporção de estreptococos do grupo mutans e na formação de cárie secundária. Para tal, 12 voluntários participaram deste estudo cruzado e duplo-cego, realizado em 3 etapas de 21 dias. Blocos de esmalte dental humano foram restaurados com CIV convencional (Ketac-fil) ou com CIV modificado por resina (Vitremer). Adicionalmente, resina (Z-100) foi usada como controle negativo. Aparelhos intra-orais palatinos, contendo quatro blocos de esmalte restaurados com um dos materiais, foram confeccionados para cada voluntário. Durante o período experimental, os voluntários usaram dentifrício não fluoretado e gotejaram solução de sacarose a 20% sobre os blocos dentais, oito vezes ao dia. Ao final de cada fase, os níveis de F, AI, cálcio (Ca), fósforo (P) e polissacarídeo insolúvel em água (PI) e as proporções de estreptococos do grupo mutans foram avaliados na placa dental coletada. Em acréscimo, o desenvolvimento de cárie secundária foi avaliado quantitativamente por meio da determinação de microdureza no esmalte adjacente às restaurações e qualitativamente por inspeção visual. Os resultados não mostraram diferenças estatisticamente significativas para as concentrações de F, AI, PI, Ca e P na placa dental, bem como para a proporção de estreptococos do grupo mutans. Por outro lado, diferenças significativas foram encontradas para a análise de microdureza e para a avaliação visual, indicando que ambos os CIVs foram capazes de diminuir a perda mineral no esmalte adjacente às restaurações. Conclui-se, portanto, que os CIVs inibiram o desenvolvimento de cárie secundária, embora - nas condições do presente estudo in situ - não tenham induzido mudanças na composição bioquímica e microbiológica da placa / Abstract: Several studies in vitro and in vivo show that glass ionomer cements (GICs) are able to reduce secondary caries. Besides, some studies have been suggesting that GICs can present inhibitory effect on cariogenic microbiota. Such effect has been attributed to some components released from the material, like fluoride (F) and aluminum (AI). Thus, the purpose of this study was to analyze biochernically and microbiologically dental plaque formed on two GICs, as well as to evaluate the effects of F and AI release on the proportion of mutans streptococci and on the formation of secondary caries. For such, twelve volunteers participated in this crossover double-blind study, performed in 3 phases of 21 days. Human enamel blocks were restored with a conventional GIC (Ketac-fil) or with a resin modified GIC (Vitremer). In addition, a resin (Z-100) was used as negative control. Intra-oral palatal appliances, containing four enamel blocks restored with one of the materiais, were constructed for each volunteer. During the experimental period, the volunteers used fluoride-free dentifrice and dripped a 20% sucrose solution onto the dental blocks, eight times a day. At the end of each phase, the levels of F, AI, calcium (Ca), phosphorus (P), water-insoluble polysaccharide (WIP) and mutans streptococci proportion were assessed in dental plaque. In addition, the formation of secondary caries was evaluated quantitatively through the determination of microhardness in enamel around the restorations, and qualitatively by visual inspection. The results did not show significant differences for the concentrations of F, AI, WIP, Ca and P in the plaque, as well as for the proportion of mutans streptococci. On the other hand, significant differences were found for the microhardness analysis and for the visual evaluation, indicating that both GICs were able to reduce the mineral loss in the enamel around the restorations. We can conclude, therefore, that GICs inhibited the development of secondary decay, although - in the conditions of the present in situ study - such materiais have not induced changes in the biochemical and microbiological composition of dental plaque / Mestrado / Cariologia / Mestre em Odontologia
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/290559 |
| Date | 18 February 2002 |
| Creators | Dalcico, Roberta |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Tabchoury, Cinthia Pereira Machado, 1969-, Pascotto, Renata Correa, Correr Sobrinho, Lourenço |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 153p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0021 seconds