The aim of this study was to understand the properties of glass/TCO/CdS/CdTe/metal solar cells, the CdS and CdTe being grown by aqueous electrodeposition. Deposited films and completed cells were characterised using electrical, structural and optical techniques. This report describes the production of well-formed polycrystalline CdS and CdTe with well defined XRD peaks and band gap. Experiments were performed to investigate the pre-conditioning of the CdTe bath on the overall cell performance. Pre-conditioning the CdTe deposition bath was found to improve the Voc value of the completed devices. It has been known for some time that treating the CdTe layer of a CdS/CdTe solar cell with chlorine brings about significant improvements in the efficiency of these devices. This report presents results on a systematic variation of the chlorine concentration within a CdTe deposition bath. Solar simulated I-V measurements of completed devices clearly show that the addition of CdCl[2] to the CdTe deposition bath significantly improved the efficiency values for the glass/TCO/CdS/CdTe/metal devices. The electrical parameter most significantly affected by the addition of chlorine is the J[sc] value. In terms of the Voc performance of the device, this investigation showed that there was a trend of improving Voc with increasing chlorine concentration. Addition of chlorine also produces improvements in the preferred orientation of CdTe films as measured by XRD. Optical absorption results showed a correlation that the minima of the band gap vs. chlorine concentration graph for annealed samples matches up with the maximum in the efficiency and J[sc] graphs. To investigate whether this phenomenon was specific to chlorine or was displayed by other elements, similar experiments were performed with no chlorine inclusion but varying the indium concentration in the deposition bath. Solar simulated I-V measurements of completed devices clearly show that the addition of In[2](SO[4])[3] to the CdTe deposition bath significantly reduced the efficiency values for the glass/TCO/CdS/CdTe/metal devices. The electrical parameter most significantly affected by the addition of indium is the J[sc] value. The addition of indium also had a detrimental effect on the preferred orientation measured by XRD.
Identifer | oai:union.ndltd.org:bl.uk/oai:ethos.bl.uk:311616 |
Date | January 1999 |
Creators | McGregor, Stephen Mark |
Publisher | Sheffield Hallam University |
Source Sets | Ethos UK |
Detected Language | English |
Type | Electronic Thesis or Dissertation |
Source | http://shura.shu.ac.uk/20043/ |
Page generated in 0.0017 seconds