This MSc. Thesis deals with electrochemical studies of the analytical utilization of self-assembled monolayers of thiolated calix[4]arene (C4A) and/or undecanthiole (C11SH) on the surface of a polycrystalline gold electrode. Hydroquinone, nitrobenzene, 2-nitrophenole and 4-nitrophenole have been used as tested model compounds. The real surface area of the electrode was determined using these two methods: From the charge of desorption peak of α-gold oxides (5.72±0.48 mm2 ) and using the Randles- Ševčík equation. (6.14±0.59 mm2 ). The preparation of the electrode consisted of polishing on alumina, immersing into piranha solution and cyclic voltammetry. The area of electrode surface was well reproducible. Stability of thiol monolayer in the area of negative potentials was tested. The C11SH layer is very stable; the desorption peak was recorded in basic solutions only (at −1.3 V vs. 3M Ag/AgCl). The position of the desorption peak of C4A is more pH dependent and it was recorded at −1.08 V at pH 13. The properties of the electrode modified by C11SH and or C4A were investigated using the model compound hydroquinone. It is assumed that the oxidation of the hydroquinone does not take place inside the C4A cavity; hence the hydroquinone molecule is too big to pass through the cavity. C11SH and C4 + C11SH act...
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:339551 |
Date | January 2015 |
Creators | Hrdlička, Vojtěch |
Contributors | Navrátil, Tomáš, Ludvík, Jiří |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.2946 seconds