Previous issue date: 1985-12-27 / CNPq / Este trabalho de laboratório procurou dar continuidade a uma serie de pesquisas que, com o decorrer do tempo,vem se desenvolvendo com as argilas esmectíticas de cores verde-clara, vermelha e do tipo sortida da localidade de Bravo,Distrito de Boa Vista, Município de Campina Grande, Paraíba, visando o estudo dos efeitos de tratamento de cura* cm algumas propriedades reológicas dessas argilas para uso como fluidos
tixotrópicos na perfuração de poços de Petróleo. De início foram feitos os ensaios de caracterização mineralógica. Posteriormente foi feita uma analise das propriedades tecnológjcas verificadas através da determinação das viscosidades aparente e plástica e do volume do filtrado nas argilas em sua forma natural. Em seguida, foram observadas as propriedadesreologicas nas argilas tratadas com carbonato de sódio na proporção de 100meq por 100g de argila seca sem tratamento de cura. Os processos de tratamento de cura foram realizados com o auxílio de uma câmara úmida e autoclave , mantendo-se
constante a concentração de carbonato de sódio e umidade relativa, e, variando-se a temperatura e o tempo. Em todas as condições estudadas foi verificado o efeito da diálise e o efeito da diálise com uso de COj. 0 uso da diálise, visa eliminar os compostos solúveis ou parcialmente solúveis de cálcio e magnésio, formados pela reação química de dupla trocapor ocasião de tratamento com o composto de sódio (montmorilonita (Mg ,Ca ,Na ,K ,11) + Na2C03 -> montmori 1 onita (Na) + MgCO^ + CaCO., + CO +llO0 + K? CO ) (|ne se pode dissolver na dispersão aquosa da argila, prejudicando as propriedades coloidais da montmorilonita , principalmente a viscosidade plástica. O uso do CO2 tem a finalidade de observar ate que ponto sua ação prejudica as propriedades reológicas das argilas em estudo. Foram determinados, igualmente, teores de carbonatos e bicarbonatos, existentes na suspensão a 6% de sólidos. Estes valores foram utilizados para explorar possíveis correlações com as viscosidades aparentes, plásticas e volume do filtrado, através da análise de regressões lineares simples e múltipla. Os resultados obtidos dos ensaios tecnológicos mostraram que as argilas de cores verde-clara, vermelha e do tipo sortida após tratamento conveniente, apresentaram excelentes propriedades reológicas, possibilitando, assim, o uso dessas argilas como agentes tixotrópicos em fluidos para a perfuração rotativa de poços de Petróleo. 0 efeito da diálise, por sua vez, tem grande influência na melhoria das propriedades reológicas para o tratamento das argilas sem processo de cura e, após o processo de cura em câmara úmida e autoclavagem ,onde
as argilas são tratadas com solução de carbonato de sódio na proporção adequada após a autoclavagem; o uso do CO2 por sua vez, influencia bastante as propriedades reológicas, que por serem solúveis, mostram tendência de flocular o sistema e consequentemente prejudicar as propriedades reológicas. Com relação as correlações obtidas de validade Limitada, tendo em vista o reduzido numero de observações realiza
das, foram obtidos coeficientes próximos de 1, mostrando que existe relação linear entre os teores de carbonatos, bicarbonatos e carbonatos mais bicarbonatos com as viscosidades aparentes e plásticas e volume do filtrado em algumas condições
de cura. / This work of laboratory aims continue a series of research work, which has been developing, using the smectites clays light green, red and mixed couloured from Bravo, District of Boa Vista,Campina Grande, Paraîra, with purpose to study the effects of treatment of cure in some rheological properties of these clays, keeping in mind its applicability as tixotropic fluids for perfuration of oil well. Inicially, the analysis of
the rheological properties was done investing from the determination of the apparent plastic viscosités and filtrate volume in the clays under it natural form. The rheological
properties of the clays were observed by the treatment of sodium carbonate at the proportion of lOOmeq per 100g of dry clay without treatment of cure. The processes of cure treatment were done in a humid chamber and autoclave keeping the concentration
of sodium carbonate and relative humidity constant and changing the temperature and time. The dialysis effect was investigated with the use of C02 at all conditions studied. The use of dialysis process has the purpose to eliminate either soluble compounds or parcially soluble of calcium and magnesium compounds or parcially soluble of calcium and magnesium compounds formed by double exchange chemical reaction by the • 2 + 2-1- +
treatment with sodium compounds (montmorilonite, Mg ,Ca ,Na , K+, H30+)+ Na2C03 - montmorilonite (Na + ) + MgC03 + CC>2 compounds (montmorilonite, Mg ,Ca ,Na ,
K+, H30+)+ Na2C03 - montmorilonite (Na + ) + MgC03 + CC>2 + H20 + K2C03) that are able to be dissolved into clays aqueous dirpèrsion so this will spoil the colloid properties of the montmorilonite, mainly the plastic viscosité. The use of CC>2 has the objective to observe the maximun point that its action will damage rheological properties of the clays in this study. Carbonates and Bicarbonates existing in the 6% solids suspension were determined. These values were used to find correlation in filtrate volume and apparent and plastic viscosites by simple and multiple linear regression analysis. results obtained from technological tests showed that light green, red and mixed coloured clays, after the treatment, presented rheological properties adequated to be used in the perforation of oil wells. However, the effects,of dialysis has considerable influence in the improvement of the rheological properties to the treatment of the clays without the cure process and after the cure process in chamber and autoclave where the clay are treated with sodium carbonate to adequade to proportion after autoclave process.; The use of CC^,however ,
has considerable influence on the rheological properties, once it being soluble, presented the tendency to floculate the system and consequently to damage the rheological properties. With relation to correlations obtained showing to be of limited validity, even to the rcdused number of observations taken; so were obtained correlations coeficients approximately one taking that there exists linear relation between amounts of carbonates and carbonates plus bicarbonates with apparent and plastic viscosites and the filtrate volume in some of the cure conditions.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/2127 |
| Date | 05 November 2018 |
| Creators | RAMOS, Rosemary Ribeiro. |
| Contributors | FERREIRA, Heber Carlos., FOSSY, Michel François., FRANÇA, Kepler Borges. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICA, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0028 seconds