Nano-scaled carbons were produced by thermal treatment of pine wood chips and bio-char. The influence of temperature, heating rate, pyrolysis time, and type and flow rate of purge gas on the production of nano-carbons was investigated. Using TEM and SEM, different carbon-based nanomaterials were observed in the prepared samples. The effect of metal ion doping on the bio-char was also investigated. Highly functionalized nano carbonaceous materials were synthesized by low temperature hydrothermal carbonization (HTC) using glucose, sucrose, xylose, and cellulose. Carbon-encapsulated iron (Fe@C) core-shell particles were also synthesized by the HTC method and used as catalyst for Fischer-Tropsch synthesis to produce liquid hydrocarbons from syngas; it showed excellent activity. Nano-structured Co-Mo carbides over several nano-sized carbon materials were prepared using the carbothermal reduction and carbothermal hydrogen reduction methods. Nano-structured Co-Mo carbides derived from Vulcan® XC-72 were used as the catalyst to produce higher alcohols.
| Identifer | oai:union.ndltd.org:MSSTATE/oai:scholarsjunction.msstate.edu:td-5192 |
| Date | 30 April 2011 |
| Creators | Yan, Qiangu |
| Publisher | Scholars Junction |
| Source Sets | Mississippi State University |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Theses and Dissertations |
Page generated in 0.005 seconds