Previous issue date: 2014-08-27 / CNPq / O ambiente construído do futuro está sendo edificado no começo de uma nova
era ecológica, a da reutilização. Nesse sentido, a utilização de resíduos como
forma alternativa de substituição do cimento em argamassas pode vir a
alcançar o patamar da sustentabilidade. A produção excessiva de resíduos de
caulim tanto no estado da Paraíba como no interior do estado do Rio Grande
do Norte vem sendo alvo de pesquisas. Os resíduos de caulim oriundos do
processo de beneficiamento do caulim classificados como resíduo grosso e
resíduo fino são descartados de forma indiscriminada no meio ambiente,
causando grande impacto ambiental e prejudicando a população circunvizinha
das pilhas de resíduos. Na tentativa de propor alternativas para a reutilização
destes resíduos e produção de materiais inovadores para os mais variados
setores da construção civil este trabalho apresenta como objetivo avaliar o
comportamento mecânico e durabilidade de argamassas incorporadas com
resíduo de caulim calcinado. A mistura utilizada foi composta por 50% de
resíduo de caulim grosso + 50% de resíduo de caulim fino, foram incorporados
em argamassas nas proporções em massa de 1:2:6 e 1:2:8 com teores de
substituição do cimento de 0%, 5%, 10%, 15%, 20% e 30%. mento de 0%, 5%, 10%, 15%, 20% e 30%. As argamassas
foram submetidas a curas distintas sendo estas, realizadas em ambiente
interno e em ambiente externo, obedecendo as idades de 30, 60, 90, 180 e 360
dias e ainda submetidas aos ensaios de durabilidade acelerada por meio dos
ciclos de molhagem e secagem. Para a incorporação deste resíduo nas
argamassas foram realizadas a caracterização física, química e mineralógica
do resíduo, assim como avaliação da temperatura de queima do resíduo para
avaliação da reatividade da pozolana. A pozolana com melhor característica
física foi determinada a uma temperatura de 800°C e a partir desta, deu-se
prosseguimento a incorporação do resíduo de caulim calcinado sob forma de
pozolana nas argamassas. Foram moldados corpos de prova cilíndricos de 50
mm x 100 mm. Os corpos de prova conforme o tipo de cura e idade foram
avaliados mecanicamente através do ensaio de resistência a compressão
simples. Amostras das argamassas foram pulverizadas em pistilo com
almofariz de porcelana e peneiradas em peneira ABNT de n°200 após o ensaio
de resistência a compressão para serem analisadas por meio das técnicas de
difratometria de raios-X, análise térmica diferencial e gravimétrica Diante dos
valores de resistência apresentados, as argamassas com substituição do
cimento pelo resíduo de caulim calcinado, podem ser classificadas de acordo
com a NBR 13281 (2001) como sendo do Tipo I com valores de resistência
mecânica ≥ 0,1 e ≤ 4,0 (MPa) e Tipo II com ≥ 4,0 e ≤ 8,0 (MPa) para ambos os
traços 1:2:6 e 1:2:8. / The built environment of the future is being built at the beginning of a new
was ecological, that of re-use. In this sense, the use of waste as
alternative way of replacing the cement in mortars can
reach the level of sustainability. Excessive production of waste from
kaolin in the state of Paraíba and in the interior of the state of Rio Grande
has been under investigation. The kaolin residues from the
processing of kaolin classified as
waste are disposed of indiscriminately in the environment,
causing great environmental impact and damaging the surrounding population
of waste batteries. In an attempt to propose alternatives for reuse
of this waste and the production of innovative materials for the most varied
sectors of construction, this paper presents the objective of evaluating the
mechanical behavior and durability of mortars incorporated with
residue of calcined kaolin. The mixture used was composed of 50%
kaolin residue + 50% fine kaolin residue, were incorporated into the
mortars in 1: 2: 6 and 1: 2: 8 mass proportions with
cement substitution of 0%, 5%, 10%, 15%, 20% and 30%. 0%, 5%, 10%, 15%, 20% and 30%. The mortars
were submitted to different cures, these being carried out in an environment
internal and external environment, obeying the ages of 30, 60, 90, 180 and 360
days and subjected to the tests of accelerated durability by means of the
wetting and drying cycles. For the incorporation of this residue in
mortars were carried out the physical, chemical and mineralogical characterization
of the residue, as well as the evaluation of the burning temperature of the residue for
evaluation of pozzolan reactivity. Pozolana with better characteristics
physics was determined at a temperature of 800 ° C and from this it was
the incorporation of the residue of calcined kaolin in the form of
pozzolan in mortars. 50 cylindrical specimens were molded
mm x 100 mm. The specimens according to the type of cure and age were
evaluated mechanically by the compressive strength test
simple. Samples of the mortars were sprayed in pistil with
porcelain mortar and sieved in No. 200 ABNT sieve after the test
compression strength to be analyzed by
X-ray diffraction, differential and gravimetric thermal analysis
values presented, mortars with
by the residue of calcined kaolin, can be classified according to the
with NBR 13281 (2001) as Type I with resistance values
mechanics ≥ 0.1 and ≤ 4.0 (MPa) and Type II with ≥ 4.0 and ≤ 8.0 (MPa) for both
traces 1: 2: 6 and 1: 2: 8.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/376 |
| Date | 12 April 2018 |
| Creators | BELTRÃO, Suellen Lisboa Dias. |
| Contributors | FERREIRA, Heber Carlos., NEVES, Gelmires de Araújo., CARTAXO, Juliana de Melo., OLIVEIRA, Djane de Fátima. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0028 seconds