Previous issue date: 2011-09-15 / O objetivo deste trabalho foi avaliar o efeito do tratamento térmico na adesão de bráquetes monocristalinos silanizados após processo de silicatização. O estudo foi autorizado pelo comitê de ética da Universidade Federal de Juiz de Fora, parecer número 161/2010. Sessenta bráquetes de alumina monocristalina (Pure®, Orthotechnology, Tampa, FL, EUA) e sessenta dentes pré-molares superiores recém extraídos com finalidade ortodôntica foram randomicamente divididos em três grupos (n=20) de acordo com a estratégia de tratamento das superfícies adesivas: G1- sem tratamento (grupo controle); G2- jateamento com partículas de alumina revestidas por sílica-30 µm Cojet (3M ESPE, Irvine, CA, EUA) + aplicação do silano Monobond S (Ivoclar Vivadent, Shaan, Liechtenstein); e G3- jateamento com Cojet seguido de silanização e tratamento térmico da superfície com jato de ar (Secador Taiff Compacto Turbo, 6000W, São Paulo, SP) à 100ºC±1, a 1 cm por 60 s. Após os tratamentos de superfície, os bráquetes foram colados aos dentes com o adesivo ortodôntico Transbond XT Light Cure Adhesive (3M ESPE, Irvine, CA, EUA). Os espécimes foram armazenados em estufa com água destilada a 37ºC por 100 dias. Durante este período, metade dos espécimes de cada grupo foi submetida à termociclagem (-T) (6000 ciclos, 5ºC±1 e 55ºC±1) com banhos alternados de 30 s. Com o auxílio de uma máquina universal para ensaios mecânicos (EMIC - DL 1000, São José dos Pinhais, Paraná, Brasil – F.O. Unesp, São José dos Campos, SP) e um dispositivo tipo faca, os grupos foram submetidos ao ensaio de resistência adesiva ao cisalhamento (1mm/min) até que ocorresse o descolamento dos bráquetes. As superfícies fraturadas foram observadas sob microscopia óptica (30×) para categorização dos tipos de falha e determinação do índice de remanescente adesivo (IRA). Doze amostras representativas (n=2) foram também observadas em microscopia eletrônica de varredura. Os resultados foram submetidos à análise estatística ANOVA (2-fatores) e as médias foram comparadas pelo teste de Tukey com nível de significância em 5% para ambos os testes. Para os resultados de resistência adesiva, o teste ANOVA revelou significância estatística para a interação dos fatores tratamento de superfície e termociclagem (p= 0,013) e para o tratamento de superfície (p= 0,0). O fator termociclagem não influenciou estatisticamente os resultados (p = 0,6974). As maiores e menores médias de resistência adesiva com o desvio padrão foram encontradas respectivamente em G3-T (27,59 ± 6,4 MPa) e G2-T (8,45 ± 6,7 MPa). Na análise da superfície após o ensaio, foi constatada a fratura de esmalte e/ou dentina em dezesseis espécimes. Com exceção do grupo G2, todos os outros apresentaram fratura de estrutura dentária. O modo de falha tipo misto e IRA = 1 (49,12%) foram os mais frequentes. Conclui-se que o tratamento térmico das superfícies silanizadas após o jateamento com partículas de alumina revestidas por sílica produziu valores de resistência adesiva similares aos valores encontrados no grupo controle. / The objective of this study was to evaluate the effect of heat treatment on bond strength of monocrystalline brackets silica coating and silanization process. The study was approved by the ethics committee of the Federal University of Juiz de Fora, autorization number 161/2010. Sixty brackets monocrystalline alumina (Pure®, OrthoTechnology, Tampa, FL, EUA) and sixty premolars recently extracted for orthodontic were randomly, divided in three groups (n=20) according to the strategy of treating surfaces adhesive: G1 – no treatment (control group), G2 – blasting with alumina particles coated with silica 30 µm Cojet (3M ESPE/ Irvine, CA, EUA) + application of silane Monobond S (Ivoclar Vivadent, Shaan, Liechtenstein), and G3 – blasting (Cojet) + silanization + heat treatment with a hairdryer (Taiff Compact Turbo Dryer, 6000W, São Paulo, SP) to 100ºC ± 1, to 1 cm, for 60 s. After surface treatments, the brackets were bonded to teeth with orthodontic adhesive Transbond XT Light Cure Adhesive (3M ESPE, Irvine, CA, EUA). The specimens were stored in distilled water for 100 days. During this period, half of the specimens of each group was subjected to thermocycling (-T) (6000 cycles, 5ºC ± 1ºC and 55ºC ± 1) with baths of 30 seconds. With the support of a universal mechanical testing machine (EMIC – DL 1000, Pinhais, Paraná, Brazil – FO/UNESP, São José dos Campos, SP) an device like a knife, the groups were submitted a shear bond strength test (1mm/min) until failure. The fractured surfaces were observed under debonded specimen surfaces were examined with a stereomicroscope (30×) to classify the types of failure and determine the adhesive remnant index (ARI). Twelve representative samples (n=2) were also observed in scanning electron microscopy. The results were statically analyzed using ANOVA (two-way) and means were compared by Tukey test with significance level of 5% for both tests. For the results of bond strength, the ANOVA revealed statistical significance for the interaction of surface treatment and thermocycling (p= 0,013) and the surface treatment (p= 0,0). The factor thermocycling did not influence the results statistically (p= 0,6974). The highest and lowest mean bond strength including the standard deviation were found in G3T (27,59 ± 6,4 MPa) and G2T (8,45 ± 6,7MPa). In the analysis of the surface after test was found sixteen specimens with enamel/dentin fracture. Except for G2, all others groups had fractured tooth structure. The failure mode mixed and IRA=1 (49,12%) were the most frequent. The heat treatment of the silanized surfaces after blasting with alumina particles coated with silica produced bond strength values similar to those found in the control group.
| Identifer | oai:union.ndltd.org:IBICT/oai:hermes.cpd.ufjf.br:ufjf/2056 |
| Date | 15 September 2011 |
| Creators | Silva, Emília Adriane |
| Contributors | Reskalla, Hélcio Nagib José Feres, Queiroz, José Renato Cavalcanti de, Pereira, Marília Nalon |
| Publisher | Universidade Federal de Juiz de Fora, Programa de Pós-graduação em Clínica Odontológica, UFJF, Brasil, Faculdade de Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFJF, instname:Universidade Federal de Juiz de Fora, instacron:UFJF |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0032 seconds