In this study, barium strontium titanate (BST) thin films with different compositions (Ba0.9Sr0.1TiO3, Ba0.8Sr0.2TiO3, Ba0.7Sr0.3TiO3, Ba0.5Sr0.5TiO3) were produced by chemical solution deposition technique. BST solutions were prepared by dissolving barium acetate, strontium acetate and titanium isopropoxide in acetic acid and adding ethylene glycol as a chelating agent and stabilizer to this solution, at molar ratio of acetic acid/ethylene glycol, 3:1. The solution was then coated on Si and Pt//Ti/SiO2/Si substrates at 4000 rpm for 30 seconds. Crack-free films were obtained up to 600 nm thickness after 3 coating & / #8211 / pyrolysis cycles by using 0.4M solutions.
Crystal structure of the films was determined by x-ray diffraction while morphological properties of the surface and the film-substrate interface was examined by scanning electron microscope (SEM).
Dielectric constant, dielectric loss and ferroelectric parameters of the films were measured. Sintering temperature, film composition and the thickness of the films
were changed in order to observe the effect of these parameters on the measured electrical properties.
The dielectric constant of the films was decreased slightly in 1kHz-1 MHz range. It was seen that dielectric constant and loss of the films was comparable to chemical solution deposition derived films on literature. Maximum dielectric constant was obtained for the Ba0.7Sr0.3TiO3 composition at a sintering temperature of 800& / #730 / C for duration of 3 hours. Dielectric constant increased whereas dielectric loss decreased with increasing film thickness.
BST films have composition dependent Curie temperature. For Ba content greater than 70 %, the material is in ferroelectric state. However, fine grain size of the films associated with chemical solution deposition and Sr doping causes the suppression of ferroelectric behaviour in BST films. Therefore, only for Ba0.9Sr0.1TiO3 composition, slim hysteresis loops with very low remanent polarization values were obtained.
| Identifer | oai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/1127679/index.pdf |
| Date | 01 January 2004 |
| Creators | Adem, Umut |
| Contributors | Ozenbas, Macit Ahmet |
| Publisher | METU |
| Source Sets | Middle East Technical Univ. |
| Language | English |
| Detected Language | English |
| Type | M.S. Thesis |
| Format | text/pdf |
| Rights | To liberate the content for public access |
Page generated in 0.1284 seconds