Interactions between copper and chlorine disinfectants were examined from the perspective of disinfectant decay and copper pitting corrosion. Sparingly soluble cupric hydroxide catalyzed the rapid decay of free chlorine, which in turn, led to production of less soluble and more crystalline phases of cupric hydroxide. The catalytic activity of the cupric hydroxide was retained over multiple cycles of chlorine dosing.
Experiments with chloramine revealed that copper species could also trigger rapid loss of chloramine disinfectant. In copper pipes, loss of free chlorine and chloramine were both rapid during stagnation. Reactivity of the copper to the disinfectants was retained for weeks. Phosphate tended to decrease the reactivity between the copper pipe and chlorine disinfectants.
A novel, inexpensive and real-time test to monitor copper pitting corrosion was developed. In a normal pipe, it is not possible to measure the electron flow or pitting current from the pit anode to the cathode. But a new method was developed that can form an active pit on the tip of a copper wire, which in turn, allows the pitting current to be measured. Preliminary experiments presented herein have proven that this technique has promise in at least one water condition known to cause pitting. The method also quickly predicted that high levels of orthophosphate could stop pitting attack in this water, whereas low levels would tend to worsen pitting. Future research should be conducted to examine this technique in greater detail. / Master of Science
Identifer | oai:union.ndltd.org:VTETD/oai:vtechworks.lib.vt.edu:10919/35674 |
Date | 09 December 2005 |
Creators | Nguyen, Caroline Kimmy |
Contributors | Environmental Engineering, Edwards, Marc A., Dietrich, Andrea M., Vikesland, Peter J. |
Publisher | Virginia Tech |
Source Sets | Virginia Tech Theses and Dissertation |
Detected Language | English |
Type | Thesis |
Format | application/pdf |
Rights | In Copyright, http://rightsstatements.org/vocab/InC/1.0/ |
Relation | CKN_Thesis_12-6-05.pdf |
Page generated in 0.0169 seconds