Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2016. / Made available in DSpace on 2016-09-20T05:04:33Z (GMT). No. of bitstreams: 1
340636.pdf: 4139989 bytes, checksum: 002f7a77d71e55c530e91bca8eab2109 (MD5)
Previous issue date: 2016 / A cementação a plasma tem sido utilizada com o intuito de melhorar a qualidade das propriedades superficiais de diferentes materiais, visto as vantagens desse processo quando comparado aos tratamentos convencionais. Normalmente, os tratamentos de cementação são realizados em altas temperaturas, levando a possíveis perdas nas tolerâncias geométricas das peças. Neste trabalho foram investigados tratamentos individuais de cementação e tratamentos sequenciais de nitretação-cementação a plasma em baixas temperaturas, em amostras de ferro puro produzidas via metalurgia do pó. Os tratamentos de cementação foram realizados a 500 °C em uma atmosfera de 98%H2 + 2%CH4, durante 3 horas. As nitretações, por sua vez, foram realizadas a 500 °C durante 3 horas em três diferentes misturas gasosas: (1%N2 + 99%H2), (10%N2 + 90%H2) e (90%N2 + 9% H2 + 1% CH4), todas seguidas por um tratamento de cementação a plasma. Parâmetros como pressão, fluxo, diferença de potencial (DDP) e tempo de pulso ligado (ton), foram mantidos constantes em todos os tratamentos. A morfologia e as propriedades das camadas cementadas foram avaliadas em função dos diferentes tratamentos de nitretação. A microestrutura das camadas foi avaliada por meio da microscopia óptica (MO) e eletrônica de varredura (MEV). Para a análise de fases foi empregada a difração de raios-x com ângulos rasantes, utilizando 1 e 3° como ângulos de incidência. A caracterização da topografia das camadas foi realizada com o auxílio da técnica de interferometria óptica de luz branca e MEV. E a dureza das camadas foi avaliada através de nanodureza e microdureza Vickers. Os resultados mostram uma influência da mistura gasosa na morfologia, e nas fases das camadas nitretadas. Uma fina camada de cementita foi observada após todos os tratamentos de cementação, tendo seu crescimento e propriedades influenciados pelas diferentes camadas nitretadas. Além disso, o tratamento sequencial de cementação elevou a dureza superficial e aumentou a profundidade de endurecimento das camadas nitretadas.<br> / Abstract: Plasma carburizing has been employed in order to improve surface properties of different materials due the many advantages offered by this process when compared to conventional carburizing techniques. Normally, these treatments are realized at high temperatures, which cause loss of dimensional tolerances. In this work plasma carburizing and plasma nitriding-carburizing of sintered pure iron at low temperatures were investigated. The carburizing treatments were performed at 500 °C for 3 hours in a mixed atmosphere of 98% H2 + 2% CH4. The nitriding treatment were perfomed at 500 °C for 3 hours in three different gas mixture: (1%N2 + 99%H2), (10%N2 + 90%H2) and (90%N2 + 9% H2 + 1% CH4) all followed by a plasma carburizing. Parameters as gas pressure and flow, potencial difference and switched-on time (ton) were kept the same in all treatments. Morphology and properties of the carburized layers have been evaluated as a function of the different nitriding treatments. The layer microstrucutures were evaluated by optical (OM) and scan electron microscopy (SEM). For phase identification, glancing angle x-ray diffraction was conducted, using 1 and 3° as incidence angles. Topography was analysed by white light optical interferometry and SEM. The layers hardness were verified by nanohardness and Vickers microhardness. Results show the influence of the gas mixture to the morphology and phase composition of the nitride compounds layers. Plasma carburizing promotes a formation of a thin and massive cementite layer. The growth and the properties of the carburized layer is influenced by the different nitrided layers. Furthemore, nitriding-carburizing treatments promote harder surface and greater case depth than single nitriding treatment.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/168223 |
| Date | January 2016 |
| Creators | Lamim, Thiago de Souza |
| Contributors | Universidade Federal de Santa Catarina, Klein, Aloisio Nelmo, Bernardelli, Euclides Alexandre |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 119 p.| il., grafs., tabs. |
| Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0024 seconds