Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2013. / Made available in DSpace on 2015-03-18T20:51:10Z (GMT). No. of bitstreams: 1
328112.pdf: 1735567 bytes, checksum: 03a5b0f8c386ab03e0cdee7fe961e4b9 (MD5)
Previous issue date: 2013 / A metalurgia do pó ferrosa é um processo que oferece inúmeras soluções na indústria, principalmente devido a economia de escala. Este processo tem algumas limitações, como o tamanho e a geometria dos corpos a serem produzidos. No intuito de investigar outras soluções para a metalurgia do pó, principalmente no condicionante a componentes, tem-se o processo de brasagem, que é a união de dois ou mais corpos, de modo a formar um corpo final único. O intuito deste trabalho é realizar a união durante a sinterização, em processo definido como sinterbonding. Para tal, estudou-se ligas de ferro cobre, com percentuais de 0 a 20% de adição de cobre, no intuito de formar fase líquida durante o processo descrito anteriormente e promover a junção de dois sólidos através do posicionamento de topo, em condições de processamento semelhantes as já aplicadas na indústria (pressão de compactação e temperatura). No intuito de caracterizar a união as amostras foram preparadas metalograficamente, para verificar a continuidade da linha da junção e também comparadas mecanicamente através de ensaio uniaxial de tração em relação a uma amostra padrão. Para melhorar os resultados também utilizou- se a técnica de recompactação. Foram obtidos tensões de ruptura 20% inferiores em relação a amostra de referência, porém com significativa redução da capacidade de deformação, de 70 a 90%.<br> / Abstract : Metal powder metallurgy is a process that offers numerous solutions in the industry, mainly due economies of scale. But this process has some limitations, such as the size and geometry of the green bodies to be produced. In order to determinate other solutions for this process, especially concerning into the geometry, it has been applied the brazing process which is the union of two or more bodies, so as to form a single body end. The aim of this work is to provide the union during the sintering process, which is defined as sinterbonding. Iron-copper alloys, with a range from 0-20% of copper where studied, in order to form a liquid phase during the process and promote the joining by top-of-body positioning, under similar conditions of those already applied in industry (pressing pressure and temperature). To characterize the union, samples were prepared metallographically to verify the continuity of the junction and also compared mechanically through tensile-strength test in reference to a standard sample. To improve the results the double pressing technique also was used. It was observed that to the samples with higher content of copper and double-pressed it was obtained better results, but if compared with a standard sample, lower mechanical strenght, a great loss in elongation and low impact resistance were obtained.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/130897 |
| Date | January 2013 |
| Creators | Becker, Rodrigo Pereira |
| Contributors | Universidade Federal de Santa Catarina, Klein, Aloisio Nelmo |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 71 p.| il., grafs. |
| Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
| Rights | info:eu-repo/semantics/openAccess |