Emprego de resíduo de silício metálico na produção de cimento portland composto / Employment of the metallic silicon residue in the production of composite portland cement

Submitted by Ivone Costa (mivone@ufpa.br) on 2018-05-18T18:52:00Z
No. of bitstreams: 2
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Dissertacao_EmpregoResiduoSilicio.pdf: 10625029 bytes, checksum: be55a09ac4e1646305f9d90ea737d824 (MD5) / Approved for entry into archive by Ivone Costa (mivone@ufpa.br) on 2018-05-18T18:53:14Z (GMT) No. of bitstreams: 2
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Dissertacao_EmpregoResiduoSilicio.pdf: 10625029 bytes, checksum: be55a09ac4e1646305f9d90ea737d824 (MD5) / Made available in DSpace on 2018-05-18T18:53:14Z (GMT). No. of bitstreams: 2
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Dissertacao_EmpregoResiduoSilicio.pdf: 10625029 bytes, checksum: be55a09ac4e1646305f9d90ea737d824 (MD5)
Previous issue date: 2017-12-19 / A reutilização de resíduos industriais e matérias primas alternativas na
construção civil é fundamental para um desenvolvimento sustentável com redução
do consumo de recursos naturais e emissões de CO2. Nesta linha, o presente
estudo contempla a utilização de um rejeito em pó, oriundo da produção do silício
metálico, o qual é designado como resíduo do pré-separador. Desta forma, é
objetivo desta pesquisa, produzir e avaliar propriedades de cimentos Portland tipo
composto CP II-E com adição, durante a sua fabricação, de resíduo industrial de
silício metálico após calcinação. Para tanto, o resíduo foi empregado em
substituição parcial à escória de alto forno, em teores em massa de 30%, 50% e
70%, além da situação de referência, o qual nenhum resíduo de silício foi
adicionado ao cimento (0%). Propriedades dos cimentos, produzidos com
resíduos, foram avaliadas quanto a sua composição química, mineralógica,
parâmetros físicos (finura, tempos de pega, perda ao fogo e resíduo insolúvel),
resistência à compressão, absorção de água, absorção por capilaridade, técnicas
microscópicas e técnicas analíticas (DR-X, composição química e análises
térmicas de TG/DTG). Como resultados, não houve diferenças significativas nos
parâmetros físicos dos cimentos produzidos. Argamassas de cimento produzidas
com maiores teores de resíduo (70% e 50%) apresentaram os maiores valores de
resistência à compressão e menores valores de absorção de água capilar, índice
de vazios e absorção de água por capilaridade que as argamassas produzidas
com cimento padrão (sem resíduo silicoso). O mesmo não foi observado para
argamassas de cimento com 30% de resíduo de silício. Técnicas analíticas de
imagens de microscopia eletrônica de varredura indicaram uma porosidade mais
fechada para argamassas de cimento nos teores de 70% e 50% de cimento com
resíduo. Assim, como conclusão, o aproveitamento do resíduo estudado como
material de substituição parcial da escória granulada em cimento composto tipo “E”
é viável tecnicamente e ambientalmente. / The reuse of industrial waste and alternative raw materials in construction
is fundamental to sustainable development with reduced consumption of natural
resources and CO2 emissions. In this line, the present study contemplates the use
of a powdered waste, originating from the production of metallic silicon, which is
designated as pre-separator residue. In this way, the objective of this research is to
produce and evaluate properties of Portland cement composite CP II-E with the
addition, during its manufacture, of metallic silicon industrial residue after
calcination. For this purpose, the residue was used in partial replacement to blast
furnace slag, in mass contents of 30%, 50% and 70%, in addition to the reference
situation, in which no silicon residue was added to the cement (0%). . Cement
properties, produced with residues, were evaluated for their chemical composition,
mineralogical, physical parameters (fineness, picking times, fire loss and insoluble
residue), compressive strength, water absorption, absorption by capillarity,
microscopic techniques and analytical techniques (DR-X, chemical composition and
thermal analyzes of TG / DTG). As results, there were no significant differences in
the physical parameters of the cements produced. Cement mortars produced with
higher residue contents (70% and 50%) had the highest values of compressive
strength and lower values of capillary water absorption, voids index and water
absorption by capillarity than mortars produced with standard cement ( without
siliceous residue). The same was not observed for cement mortars with 30% silicon
residue. Analytical techniques of scanning electron microscopy images indicated a
more closed porosity for cement mortars in the contents of 70% and 50% of cement
with residue. Thus, as a conclusion, the utilization of the residue studied as partial
replacement material of granulated slag in composite cement type "E" is technically
and environmentally feasible.

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.ufpa.br:2011/9875
Date19 December 2017
CreatorsCUNHA, Rodrigo Rodrigues da
ContributorsMACÊDO, Alcebíades Negrão
PublisherUniversidade Federal do Pará, Programa de Pós-Graduação em Engenharia Civil, UFPA, Brasil, Instituto de Tecnologia
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis