Previous issue date: 2013-08-30 / CAPEs / Existem resíduos de processos industriais que são característicos do estado de Pernambuco,
como o bagaço de cana-de-açúcar, e que são poucos abordados por estudos sistemáticos para
o seu emprego na construção civil. O estudo consiste em comparar a atividade pozolânica da
cinza do bagaço de cana-de-açúcar (CBCA) e de um material comprovadamente pozolânico
fazendo uso dos ensaios tradicionais de determinação de atividade pozolânica. Existem
diversos métodos considerados tradicionais, geralmente divididos nos que mensuram um
parâmetro de resistência mecânica (definidos como “métodos físicos”) e nos que mensuram
de forma direta ou indireta a reação química que caracteriza a existência da atividade
pozolânica (definidos como “métodos químicos”). A abordagem desta questão será utilizar
métodos físicos previstos por normas brasileiras e métodos físicos modificados para a
determinação da atividade pozolânica. No intuito de apontar caminhos para a utilização deste
resíduo na construção civil, o presente trabalho apresenta os resultados da análise de 29
amostras de cinza que receberam diferentes tratamentos térmicos e físicos e mais a análise do
metacaulim que foi utilizado como material pozolânico de referência. Todas as amostras
foram caracterizadas por difração de raios-X e passaram pelos ensaios mecânicos previstos
nas normas NBR 5751:1992 e NBR 5752:1992 para determinação do índice de atividade
pozolânica.De acordo com os resultados obtidos, evidenciou-se que os métodos normatizados
não apresentam respostas totalmente congruentes, pois, a atividade pozolânica foi constatada
pelo método de atividade com cimento Portland (IAP), porém não foi constatada pelo método
de atividade com cal hidratada. A CBCA “in natura” apresentou IAP superior ao estabelecido
pela NBR 12653:1992 (75%) quando do aumento do grau de moagem, assim como a CBCA
calcinada a 600ºC. A moagem mostrou ser de fundamental importância para o aumento do
potencial pozolânico da CBCA, concluindo-se que finura Blaine deve ser superior a 500
m2/kg. A temperatura de calcinação se mostrou relevante quando aplicação de 600ºC, acima
deste valor ocorreu o decréscimo dos índices de pozolanicidade. / There are residues of industrial processes that are characteristic of the state of Pernambuco, as
bagasse from sugar, and few addressed by systematic studies for your construction jobs. The
study is to compare the pozzolanic activity of bagasse ash from sugar cane (CBCA) and a
pozzolanic material shown making use of traditional tests to determine pozzolanic activity.
Several methods are considered traditional, generally divided in that measure a parameter of
mechanical resistance (defined as "physical methods") and in that measure directly or
indirectly the chemical reaction that characterizes the existence of pozzolanic activity (defined
as "chemical methods"). The approach to this issue is to use physical methods provided by
modified for the determination of pozzolanicity Brazilian standards and physical methods. In
order to point out ways to use this waste in construction, this paper presents the results of
analysis of 29 samples of gray that received different thermal and physical treatments and
more analysis that metakaolinpozzolanic material was used as reference. All samples were
characterized by X-ray diffraction and passed by the expected in NBR 5751:1992 and NBR
5752:1992 standards for determining the pozzolanic activity index mechanical tests.
According to the results, it was evident that standardized methods have not fully congruent
answers, because the pozzolanic activity was observed by the method of activity with
Portland (IAP) cement, but was not detected by the method of activity with hydrated lime.
The CBCA "in natura" made higher than in theNBR 12653:1992 (75%) while increasing the
fineness of grind, and calcined at 600°C CBCA IAP. The grinding proved to be of
fundamental importance to increase the potential of pozzolanic CBCA, concluding that Blaine
fineness must be greater than 500 m2 / kg. The calcination temperature was also relevant
when applying 600°C, above this value was decreasing rates of pozzolanicity.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpe.br:123456789/17103 |
| Date | 30 August 2013 |
| Creators | VASCONCELOS, Marcela Correia de Araújo |
| Contributors | http://lattes.cnpq.br/9191655335324358, CARNEIRO, Arnaldo Manoel Pereira |
| Publisher | Universidade Federal de Pernambuco, Programa de Pos Graduacao em Engenharia Civil, UFPE, Brasil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Breton |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFPE, instname:Universidade Federal de Pernambuco, instacron:UFPE |
| Rights | Attribution-NonCommercial-NoDerivs 3.0 Brazil, http://creativecommons.org/licenses/by-nc-nd/3.0/br/, info:eu-repo/semantics/openAccess |
Page generated in 0.0023 seconds