This thesis describes a study of the low temperature specific heat of LiⅹNbS₂, where x is between 0 and 1. Samples were prepared by intercalating lithium into niobium disulfide in electrochemical cells. Structural data obtained by x-ray diffraction are presented. These, together with electrochemical measurements, show that staged phases exist for some values of x. The electronic specific heat of LiⅹNbS₂, is consistent with complete charge transfer from the intercalated lithium to the bands of the NbS2 host. The lattice specific heat also shows large changes as a function of x. A discussion of the data in terms of continuum elasticity theory suggests that intercalation produces large changes in the shear elastic constant C₄₄ . A brief discussion of superconductivity in LiⅹNbS₂, is also included. / Science, Faculty of / Physics and Astronomy, Department of / Graduate
Identifer | oai:union.ndltd.org:UBC/oai:circle.library.ubc.ca:2429/25563 |
Date | January 1985 |
Creators | Dahn, Douglas Charles |
Publisher | University of British Columbia |
Source Sets | University of British Columbia |
Language | English |
Detected Language | English |
Type | Text, Thesis/Dissertation |
Rights | For non-commercial purposes only, such as research, private study and education. Additional conditions apply, see Terms of Use https://open.library.ubc.ca/terms_of_use. |
Page generated in 0.0018 seconds