Orientador: Iris Concepcion Linares de Torriani / Tese (doutorado) - Universidade Estadual de Campinas, Instituto de Fisica Gleb Wataghin / Made available in DSpace on 2018-08-08T13:36:14Z (GMT). No. of bitstreams: 1
Aguero_OscarEnrique_D.pdf: 9568417 bytes, checksum: db4b9632a94f1d1cb2691c4eeb1404ec (MD5)
Previous issue date: 2007 / Resumo: Uma serie de compostos ineditos ou pouco estudados foram sintetizados e as propriedades físicas foram estudadas usando difração de raios X e medidas magneticas em função da temperatura. Neste tipo de compostos as propriedades estruturais estão fortemente correlacionadas com as propriedades magnéticas e de transporte. Neste trabalho apresentaremos a síntese, caracterização estrutural e magnética de ligas metálicas nanoestruturadas de Cu-Fe, compostos intermetálicos R3M4Sn13(R= terra rara, M= Co e Ir), e cobaltitas (Nd1-xC axCoO3 e GdBaCo2O5,5).
Parâmetros de cela, tamanho de domínios e tensões de ligas nanoestruturadas Cu1-xFex (0<x<0,5) preparadas por ball-milling foram determinados usando difração de pó. Todos as amostras apresentam a estrutura FCC do Cu. Os parâmetros de cela aumentam com x. Usando métodos de análise do perfil de difração (largura integrada e Warren-Averbach), determinamos o tamanho dos domínios cristalinos e tensões na rede. O tamanho dos domínios decresce e as tensões aumentam com x.
As estruturas cristalinas dos compostos R3M4Sn13(R= terra rara, M= Co e Ir) foram determinadas por difração de monocristais à temperatura ambiente. Todos os compostos R3C o4Sn13 e Eu3I r4Sn13 cristalizam com uma cela cúbica Pm-3n, com parâmetros de cela a~ 9,5- 9,8 Å. Os compostos R3I r4Sn13 (R= La, Ce, Pr, Nd) apresentam uma superestrutura cúbica de corpo centrado com a¿~2a. Os compostos de Yb e Eu mostram um comportamento anômalo associado a um estado de valência diferente das outras terras raras. Estudos de difração de pó a baixas temperaturas para os compostos R3Co4Sn13 (R= La, Ce, Pr, Nd e Gd) mostram uma transição abaixo de T=150 K para uma superestrutura cúbica de corpo centrado com parâmetro de cela a¿~2a. Os compostos R3Ir4Sn13 não apresentam transições de fase até 20 K.
As propriedades estruturais e magnéticas das cobaltitas Nd1-xCaxCoO3 (0 =x =0,4), foram estudadas usando difração de pó, magnetização dc e susceptibilidade ac em função da temperatura (2-800 K). Todos os compostos cristalizam com uma estrutura ortorrômbica (Pnma) no intervalo de temperatura estudado (20-800 K). Para x =0,1 o sistema mostra um comportamento paramagnético até 2 K, com os íons Co3+ e Co 4+ em estados de baixo spin (LS) para T<180 K. Para 0,2 =x =0,4, duas transições magnéticas são observadas para T<60 K. Estas transições estão associadas a estados de "spin glass" ou "cluster glass". Um diagrama de fases magnéticas e de estados de spin foi construído e comparado com outros sistemas similares.
Foi realizada a síntese do composto GdBaCo2O5,50 e estudadas as propriedades estruturais e de transporte em função da temperatura (2-800 K). Sucessivas transições de fase magnéticas foram observadas a: TPM= 70 K, TN~ 260 K; TC~ 273 K. Observamos uma transição metal isolante a TMI~ 360 K, simultânea com uma transição de spin dos íons de Co3+ . Os resultados magnéticos são compatíveis com estados de spin: 50%Co3+ (IS)+50% Co3+ (LS) para T<TMI e 50% Co3+ (IS)+50% Co3+ (HS) para T > TMI. Estudos estruturais usando difração de pó com fonte convencional e luz de síncrotron, mostram que a TMI uma transição de spin LS ÎHS ocorre para os íons Co3+ nos octaedros. Uma transição ortorrômbica-tetragonal, de tipo ordem-desordem, foi observada a TOD~ 760 K / Abstract: A series of new compounds have been synthesized and their physical properties studied using X-ray diffraction and magnetic measurements as a function of temperature. In this type of compounds, structural properties are strongly correlated with their magnetic and transport properties. In this work we present details of the synthesis as well as the structural and magnetic characterization of nanostructured metallic alloys (Cu-Fe), intermetallic compounds of the type R3M4Sn13 (R=rare earth, M= Co, Ir), and the cobaltates Nd1-xCaxCo03 and GdBaCo2O5,5.
The lattice parameters, crystallite size and lattice strain of nanostructured Cu1-xFex(0< x <0,5) alloys prepared by the ball milling method were determined from X-ray powder diffraction analysis. All samples present the Cu FCC structure. The lattice parameter of the Cu1-xFex phases increases with x. The X-ray diffraction peaks were analyzed using the Warren-Averbach and Integral Breadth methods. The crystallite size decreases and the lattice strain increases with Fe concentration.
Crystal structures of the R3M4Sn13 (R= rare earth, M=Co, Ir) intermetallic compounds were determined from single crystal X-ray diffraction at room temperature. All R3Co4Sn13 and Eu3Ir4Sn13 compounds crystallize in the cubic Pm-3n space group with cell parameters a~9,5-9,7 ÿ. The R3IrSn13(R= La, Ce, Pr, Nd) compounds present a body centered cubic superstructure with aÂ' ~2a. In this series, the Yb and Eu compounds exhibit an anomalous behavior associated to valence states different from those of the other rare earths. Low temperature X-ray powder diffraction studies for R3Co4S n13(R= La, Ce, Pr, Nd and Gd) show a phase transition below 150 K from a simple cubic to a body centered cubic superstructure with cell parameter aÂ'~ 2 a. The temperature of the phase transition decreases with the rare earth ionic radii. No phase transitions were observed for the R3Ir4Sn13 series for temperatures down to 20 K.
The structural and magnetic properties of the cobaltates Nd1-xCaxCoO3(0 =x =0,4), were studied using powder X-ray diffraction, dc magnetization and ac susceptibility measurements as a function of temperature (2-800 K). All compounds crystallize with an orthorhombic (Pnma) structure in the temperature range (20- 800 K). For x =0,1 the Nd1-xCaxCoO3system shows a paramagnetic behavior down to 2 K, with the Co3+e Co4+ions in low spin state (LS) for T<180 K. For 0,2 =x =0,4, two magnetic transitions were observed for T<60 K. These transitions are associated to a spin or cluster glass states. A magnetic phase and spin state diagram was constructed for comparison with similar systems.
The compound GdBaCo2 O5.50was synthesized and the structural and transport properties were studied as a function of temperature [2-800 K]. Successive magnetic phase transitions were observed: TPM= 70 K, TN~ 260 K; TC~ 273 K. A metal-insulator transition is observed at TMI~ 360 K, with a simultaneous spin transition of the Co 3+ions. The magnetic measurements results are compatible with the spin states 50%Co3+(IS)+50% Co3+(LS) for T<TMI and 50%Co3+(IS)+50%Co3+(HS) for T>TMI. Structural studies using powder diffraction with a conventional X-ray source and synchrotron radiation show that the LS Ã?HS spin state transition occurs only for the Co3+ions in the octahedrons. An orthorhombic-tetragonal transition of the order-disorder type was observed at TOD~ 760 K / Doutorado / Física da Matéria Condensada / Doutor em Ciências
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/277973 |
Date | 15 May 2007 |
Creators | Aguero, Oscar Enrique |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Torriani, Iris Concepcion Linares de, 1934-, Ellena, Javier Alcides, Rettori, Carlos, Santos, Carlos de Oliveira Paiva, Cerdeira, Fernando |
Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Física Gleb Wataghin, Programa de Pós-Graduação em Física |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | 131f. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0023 seconds