Previous issue date: 2015-08-31 / Capes / As Ligas com Memória de Forma (LMF) constituem uma classe de materiais metálicos que possuem a capacidade de recuperar uma deformação pseudo plástica, introduzida por aplicação de carga mecânica, e retornar à sua forma original através de um simples aquecimento. O principal interesse nos atuadores de LMF utilizados no formato de molas helicoidais reside no grande deslocamento proporcionado pelo fenômeno de Efeito Memória de Forma (EMF), que permite a realização de trabalho mecânico quando este componente é submetido a diferentes condições de temperatura e cargas mecânica. No caso de elementos de LMF em estado de superelasticidade (SE) na temperatura ambiente, quando a carga mecânica é aplicada e mantida sob o material, a deformação originada pela formação de martensita induzida por tensão poderá também ser revertida por meio de um aquecimento. Nesse caso, tem-se um EMF em um elemento de LMF originalmente superelástico. Nesse contexto, o objetivo deste trabalho é realizar a caracterização eletromecânica de uma mini mola superelástica de LMF NiTi (Nitinol) quando submetida a um carregamento mecânico constante, avaliando a influência da taxa de variação da corrente elétrica e do aumento da carga mecânica nas temperaturas de transformação, além de determinar o comportamento do deslocamento com a variação de resistência elétrica. Para isso, foi desenvolvida uma plataforma experimental capaz de submeter a mini mola a carregamento mecânico constante (peso) e sinais de corrente elétrica variáveis com o tempo. Verificou-se que, para todas as cargas mecânicas e níveis de corrente elétrica, os resultados para a taxa de variação da corrente elétrica mais lenta (6 mA/s) apresentou uma melhor resposta em deslocamento e na variação da resistência elétrica quando comparados com a taxa mais rápida (12 mA/s), embora esta última resulte em um comportamento histerético mais estreito (resistência elétrica versus deslocamento). Também foi observado um aumento das temperaturas de transformação com o aumento da carga mecânica, como esperado pela lei de Clausius-Clayperon para LMF. Finalmente, foi verificada uma relação praticamente linear entre a variação do deslocamento e a variação de resistência elétrica, no aquecimento e no resfriamento. / The Shape Memory Alloys (SMA) are a class of metallic materials that have the ability to recover pseudo plastic deformation introduced by the application of mechanical load, and return to original shape by heating. The main interest in the SMA actuators used in the form of coil springs lies in the large displacement provided by the shape memory effect (SME) phenomenon, which allows performing mechanical work when the component is subjected to varying conditions of temperatures and mechanical loads. In the case of SMA elements in a state of superelasticity (SE) at room temperature, when mechanical load is applied and maintained on the material, the deformation caused by the formation of stress induced martensite can be reversed by heating. In this case, we have a SME in a SMA element originally superelastic. In this context, the objective of this work is to realize the electromechanical characterization of a superelastic mini coil spring of Ni-Ti SMA (Nitinol), when subjected to a constant mechanical loading, evaluating the influence of the electric current rate, the influence of mechanical load on the phase transformation temperatures, and determining the displacement behavior to the variation of electrical resistance. For this, an experimental platform was developed to submit the mini spring under constant load (dead weight) to electric current signals varying with time. It was found that for all mechanical loads and electrical current levels, the results for the slower rate of change electrical current (6 mA/s) showed a better response in displacement and the variation in the electrical resistance when compared to faster rate (12 mA/s), although the faster rate present a narrower hysteretic behavior (electrical resistance vs displacement). There was also verified an increase in phase transformation temperatures with increased mechanical load, as expected by the Clausius-Clayperon law for SMA. Finally, a practically linear relationship was found between the change in displacement with the variation in electrical resistance, during heating and cooling.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/453 |
| Date | 23 April 2018 |
| Creators | MONTEIRO , Roana d’Ávila Souza. |
| Contributors | FERNANDES , Eisenhawer de Moura., ARAÚJO , Carlos José de., ROCHA NETO, José Sérgio da., SOUTO, Cícero da Rocha. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0028 seconds