Orientador: Altair Antoninha Del Bel Cury / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-20T17:02:17Z (GMT). No. of bitstreams: 1
Rodrigues-Garcia_RenataCunhaMatheus_D.pdf: 2889884 bytes, checksum: a95426c1f4c9cf7fb15fbe65551ab547 (MD5)
Previous issue date: 1995 / Resumo: Este estudo verificou a adaptação e porosidade de bases de prótese submetidas a um duplo ciclo de polimerização. Foram confeccionados 36 modelos em gesso pedra a partir de moldagem de um modelo-mestre metálico. Esses modelos foram divididos em 03 grupos de 12 elementos cada. Bases de resina acrílica convencional foram confeccionadas sobre os modelos dos grupos 1 (G 1) e 2 (G2), polimerizados em banho de água durante 9 horas a 730 C; e bases de resina específica para microondas foram construídas sobre os modelos do grupo 3 (G3) e curadas em fonlO de microondas a 500W durante 3 mino A adaptação foi verificada através do peso de um material de impressão interposto entre a base da resina e o modelo mestre sob carga de 2 Kg. A seguir todas as bases foram reembasadas pelo método de adição, sendo que aquelas dos grupos 1 e 3 foram reembasadas com o mesmo material e técnica de polimerização. As bases do grupo 2 foram preenchidas com a mesma resina, porém curadas em fonlO de microondas a 500W durante 3 mino A adaptação foi reavaliada da maneira descrita acima. A porosidade foi verificada através de imersão das amostras polidas em tinta preta, e os poros contados em lupa esteroscópica com aumento de 63x. As médias e desvios-padrão obtidos para a adaptação antes e após o reembasamento foram: G 1: 0,632 + 0,024 - 0,659 + 0,026; G2: 0,632 :t 0,033 - 0,677 + 0,031; G3: 0,580 + 0,019 - 0,798 + 0,049, sendo que houve diferença sigllificante apenas para o G3. As médias e desvio-padrão para a porosidade antes e após o reembasamento for'!ffi respectivamente: G 1 = 8,33 + 0,69 - 9,25 + 0,85; G2 = 8,17 + 0,98 - 10,08 + 1,63; G3 = 5,42 + 0,78 - 6,58 + t02, sendo que não houve diferenças significantes entre os grupos estudados após o reembasamento. Conclui-se que a resina convencional, quando polimerizada no primeiro ciclo pelo método convencional e no segundo ciclo através de energia de microondas, apresentou adaptação semelhante ao método convencional de reembasamento. Em relação à porosidade foi verificado que, tanto após o primeiro como o segundo ciclo de cura, a resina convencional apresentou maior número de poros / Abstract: In this study was verified the accuracy and porosity of denture submitted for double cycles of polymerization. Thirty six mas ter cast were made in dental stone from the impression of metal die. These master cast were divided by three groups of 12 elements each. Denture bases of conventional acrylic resin were made on the casts of the groups I e II (GI and GIl), polymerized in water bath duril1g 9 hours at 730C, and specific resin for denture bases for microwave polymerization were made on the casts of group III (GllI) and cured in microwave oven at 500W during 3 minutes. The accuracy was verified by the weight of a impression material was put between the denture base and cast die under load of 2 Kg. Afterwards, all the denture bases were relining by addition method, and those of the group 1 and III were relined with the same material and polymerization tech.l11c. The denture bases of the group II were filled with the same resin, however cured in microwave oven with 500W during 3 mil1utes. The accuracy was
revaluable by the same way as described above. The porosity, was verified by the immersion of the polish specimens in a solution of pennanent black i.nk and the pores were counted through a stereo light microscope with under magnification of 6,3 x. The average and standard deviation gotten for an accuracy before and after the relinil1g were respectively: G 1: 0,632 + 0,024 - 0,659 + 0,026; G2: 0,632 + 0,033 - 0,677 + 0,031; G3: 0,580 + 0,018 - 0,798 + 0,049. There was a significant difference only for the group TIl. The average and standard deviatio.l1 for the porosity before and after the relining were respectively: Gl = 8,33 + 0,63 - 9,25 + 0~85; G2 = 8,17 + 0,98 + 10,08 + 1,63; G3 = 5,42 + 0,78 - 6,58 + 1,02. The concluslon is that the conventional resin when polymerizated in the fust cycle by conventional method and in the second cycle by microwaves energy showed similar accuracy to conventional relining. ln relatiori to the porosity was verified that as after the fust and second cycle of polymerization, the conventional resin showed the highest number of pores / Doutorado / Protese Dental / Doutor em Odontologia
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288201 |
Date | 28 September 1995 |
Creators | Rodrigues-Garcia, Renata Cunha Matheus, 1964- |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Del Bel Cury, Altair Antoninha, 1948-, Panzeri, Heitor, Bonachella, Wellington Cardoso, Silva, Frederico Andrade e, Goes, Mario Fernando de |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | 107f. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0023 seconds