Orientador: Sergio Gama / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Fisica Gleb Wataghin / Made available in DSpace on 2018-07-22T19:19:49Z (GMT). No. of bitstreams: 1
Urbano_Alexandre_M.pdf: 2101753 bytes, checksum: 1a1f1b27f655da85618c1912781e5e0c (MD5)
Previous issue date: 1997 / Resumo: Filmes finos das fases Fe17TR2, TR = terras raras, são de muito interesse devido as boas propriedades magnéticas que estes materiais possuem na forma de "bulk". Na forma de filmes finos estas propriedades são mantidas, e filmes podem exibir anisotropia magnética perpendicular e altas coercividades.
Nossas amostras de Fe17TR2, TR = Nd, Pr, e Sm, foram preparadas principalmente por "flash evaporation", sendo necessário para isto a preparação do material em '"bulk". Os compostos contendo Pr e Nd foram preparados por fusão à arco, em atmosfera inerte de argônio, seguido de tratamento térmico a 1000°C por 10 dias. As amostras foram então trituradas e peneiradas até a espessura de 200 mesh. Para aterra rara Sm, utilizamos um composto já preparado conseguido junto a Goldschmidt Co, que foi peneirado até a mesma dimensão. Para Pr, Nd, e Sm, obtivemos filmes por "flash evaporation" em uma unidade de evaporação Balzers, usando Ta e W como fontes de evaporação. A pressão de deposição foi tipicamente de 10-6 Torr. Para aterra rara samário filmes foram produzidos também por DC "sputtering", utilizando um alvo sinterizado com o material da Goldschmidt CO. Para ambas as técnicas de deposição vários substratos foram testados, como: vidro, vidro recoberto com CaF2 (500Å), alumina, tantalo e cobre laminado. A espessura dos nossos filmes foram de 3.000 à 5.000 Å, medidos por perfilometria e interferometria.
Após as deposições os filmes foram tratados termicamente em um forno de lâmpadas sob atmosfera inerte de argônio em temperaturas de 300°C a 700°C. O tempo de tratamento variou de 10 a 180 min. Depois do tratamento térmico a amostra era submetida a uma atmosfera de nitrogênio sob 400°C, por 10 min. Este procedimento de nitrogenação foi feita no forno de lâmpadas.
As amostras como depositadas e como tratadas termicamente foram analisadas por difratometria de raios-X, e uma Microanálise Eletrônica foi feita para assegurar a proporção dos elementos do composto. As propriedades magnéticas foram determinadas por um Magnetômetro de Amostra Vibrante, e um Analisador Termo-Magnético / Abstract: Films of the Fe17R2Nx phases, R= rare-earthsf are interesting because of the good magnetic and properties these materiais have in bulk form, mainly for R from = Sm, that show axial magnetic anisotropy .In film form these good magnetic properties are maintained, and films can show perpendicular anisotropy high coercivities.
For Pr and Nd the bulk material was prepared by arc-melting the components in argon atmosphere, followed by heat treatment at 1000ºC/10 days. The samples were then crushed and sieved down to 200 mesh. For the Sm, we used powder obtained from Goldschmidt Co, sieved to the same size. For Pr, Nd and Sm, films were obtained by flash evaporation in a Balzers deposition unit, using Ta and W heated boats. Base pressure prior to deposition was typically 10-6 torr. For the samarium case we used also a DC sputtering apparatus using a sintered target built with powder from Goldschmidt Co. For both deposition techniquesf several substrate materiais were attempted, as glass, glass covered with a CaF2 buffer layer of 500 Å, aluminaf tantalum foil and laminated copper. Thicknesses were measure using a stillus perfilometer, and ranged from 3.000 to 5.000 Å.
After deposition, t films were heat-treated in a lamp furnace under high purity argon. Temperatures ranged from 300ºC up to 750ºC, by 10 until 180 min. After the heat-treatment we did nitrogenation of the films in the same lamp furnace, at 400ºC, during 10 min, under an one atm high purity nitrogen atmosphere.
The as-prepared, heat-treated and nitrogenated samples were characterized by x-ray diffraction. Electron microprobe analysis was used to assure that the right proportion of the elements was in the samples. The magnetic properties were determined using a vibrating sample magnetometer (VSM) and an AC thermomagnetic analyser (TMA) / Mestrado / Física / Mestre em Física
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/277137 |
| Date | 06 June 1997 |
| Creators | Urbano, Alexandre |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Gama, Sergio, 1949-, Cabral, Francisco de Assis Olimpio, Morais, Mario Antonio Bica de |
| Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Física Gleb Wataghin, Programa de Pós-Graduação em Física |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 82f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0013 seconds