Previous issue date: 2017-09-01 / O processo de secagem consiste na remoção de umidade de um material através do aquecimento, envolvendo mecanismo simultâneo de transferência de calor e massa entre o material e o ar de secagem, sendo uma importante etapa na conformação de um material cerâmico e argiloso. Neste sentido, este trabalho objetiva a simulação da secagem de sólidos vazados e com forma arbitraria. Para descrever o processo de secagem de materiais porosos utilizou-se o método da capacitância global. A aplicação tem sido feita para a secagem de materiais cerâmicos afim de obter resultados cinéticos de perda de massa e calor dos mesmos. Foram simulados diferentes casos variando-se a forma do corpo, de onde obteve-se as cinéticas de secagem (perda da umidade) e aquecimento do sólido (aumento de temperatura). Observou-se que o processo de perda de umidade ocorre numa menor velocidade que o aquecimento do material cerâmico, pois a sua difusividade térmica é muito superior a difusividade de massa, e que o formato do sólido, particularmente a sua relação área/volume afeta fortemente os fenômenos de transporte de calor e massa. / The drying process consists of the removal of moisture from a material through heating,
involving simultaneous heat and mass transfer between the material and the drying air, being an important step in the formation of a clay and ceramic material. In this sense, this work aims at simulating the drying of cast and cast solids. To describe the drying process of porous materials, the global capacitance method was used. The application has been made for the drying of ceramic materials in order to obtain kinetic results of loss of mass and heat of the same. Different cases were simulated by varying the shape of the body, from which the kinetics of drying (loss of moisture) and heating of the solid (temperature increase) were obtained. It was observed that the process of moisture loss occurs at a slower rate than the heating of the ceramic material, because its thermal diffusivity is much higher than mass diffusivity, and that the shape of the solid, particularly its area / volume ratio strongly affects The phenomena of heat and mass transport.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/371 |
| Date | 12 April 2018 |
| Creators | LIMA, Wanderson Magno Paiva Barbosa de. |
| Contributors | FARIAS NETO, Severino Rodrigues de., CAVALCANTI, Wilma Sales., FARIAS, Fabiana Pimentel Macêdo. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0029 seconds