Previous issue date: 2017-04-24 / Neste trabalho, foram estudadas as propriedades físicas, mecânicas, acústicas e térmicas de um traço de Concreto autoadensável (CAA) já utilizado por uma Usina de Concreto, e outros três traços com substituição de cimento Portland (CP) por Cinza de casca de arroz (CCA). O traço referência (sem substituição) foi utilizado na construção de um Edifício de parede de concreto. Os ensaios foram definidos a fim de ser possível a análise tanto da resistência à compressão e resistência à tração diametral, quanto o conforto térmico e acústico apresentado por esse material, quando comparado com o que é normatizado. Para isso, foram realizados os ensaios no estado fresco, garantindo as especificações de todas as propriedades exigidas para um concreto ser considerado autoadensável. Após essa caracterização, moldaram-se os corpos de prova necessários para todos os ensaios do estado endurecido, sendo corpos de prova cilíndricos (100x200mm) para ensaios mecânicos, cilíndricos (20x100mm) para ensaios acústicos e retangulares (300x300x100mm) para ensaios térmicos. No quesito de resistência à compressão, superou o fck estabelecido aos 28 dias, que era de 25 MPa. Analisando os valores encontrados para absorção e isolamento acústico, pode-se dizer que apresentaram resultados satisfatórios na menor faixa de frequência e, na maior, apresentaram alguns problemas que acredita-se serem referentes ao equipamento utilizado. No desempenho térmico, todos os traços, apresentaram resultados próximos entre si e a outros estudos da bibliografia e normas, não sendo influenciado pela substituição da CCA. Os resultados dos ensaios demonstraram que é possível substituir CP por CCA sem que haja prejuízo às características mecânicas os CAAs, e ainda obter ganhos econômicos. O melhor concreto, levando em conta todos os aspectos estudados, foi com 20% de substituição de CP por CCA. / In this work the physical, mechanical, acoustic and thermal properties of a Self-consolidating concrete (SCC) mix design already used by a concrete plant and others three mix design with Portland cement (PC) replacement by Rice husk ash (RHA) were studied. The reference mix design (without replacement) was used in the construction of a concrete wall building. The experimental tests were defined in order to allow the analysis of both the compressive strength and diametral tensile strength, as well as the thermal and acoustic comfort presented by this material, Thus, the tests were realized in the fresh state, guaranteeing the specifications of all properties required for a concrete to be considered self-consolidating. After this characterization, the necessary specimens were molded for all the hardened state tests, being cylindrical specimens (100x200mm) for mechanical tests, cylindrical (20x100mm) for acoustic tests and rectangular (300x300x100mm) for thermal tests. The compressive strength exceeded the fck established at 28 days, which was 25 MPa. Analyzing the values found for absorption and acoustic insulation, it can be said that they presented satisfactory results in the lower frequency range and, in the higher, presented some problems that are believed to be referring to the equipment used. In the thermal performance, all the mix design present close results among themselves and other studies of the bibliography and norms, not being influenced by replacement of the RHA. The tests results demonstrated that it is possible to replacement PC for RHA without impairing the mechanical features of the SCCs as well as to obtain economic gains. The best concrete, taking into account all aspects studied, was with a 20% replacement of PC for RHA.
Identifer | oai:union.ndltd.org:IBICT/oai:10.1.0.46:riu/1953 |
Date | 24 April 2017 |
Creators | Padoin, Daniela Galiotto |
Contributors | Kosteski, Luis Eduardo |
Publisher | Universidade Federal do Pampa, Mestrado Acadêmico em Engenharia, UNIPAMPA, Brasil, Campus Alegrete |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Repositório Institucional da UNIPAMPA, instname:Universidade Federal do Pampa, instacron:UNIPAMPA |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0021 seconds