Orientadores: Rosa Cristina Cecche Lintz, Luísa Andréia Gachet Barbosa / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Tecnologia / Made available in DSpace on 2018-08-28T13:32:52Z (GMT). No. of bitstreams: 1
Verzegnassi_Emerson_M.pdf: 3873734 bytes, checksum: 73682762affd1136f183e9120a07a536 (MD5)
Previous issue date: 2015 / Resumo: Com a descoberta de aditivos químicos e adições minerais muitos tipos diferentes de concreto surgiram ao longo das últimas décadas. Porém o peso próprio do concreto convencional é considerado a sua maior desvantagem. Com isso abre-se campo para um material que apesar de ser conhecido pelos romanos, era pouco utilizado, o concreto com agregados leves. Muitas pesquisas surgem e em aproximadamente duas décadas aparece o concreto autoadensável e mais recentemente o concreto leve autoadensável. Este trabalho propõe o estudo deste material ainda pouco explorado o concreto leve autoadensável. Para isso são produzidos concretos com argila expandida em duas granulometrias diferentes: uma graúda em substituição total ao agregado graúdo de massa normal e uma miúda em substituição parcial ao agregado miúdo. São elaboradas três famílias de traços de concreto com consumos diferentes de cimento, 320, 360 e 440 kg/m³ de concreto, e realizados ensaios no estado fresco (anel J, funil V e caixa L) e endurecido (resistências à compressão e à tração, determinação do módulo de elasticidade, absorção e densidade). Os concretos leves foram classificados como auto adensáveis e apresentaram bons resultados quanto ao fator de eficiência e resistência sendo possível estabelecer equações de correlação para seu módulo de elasticidade. Para os ensaios de densidade observaram-se concretos leves com massas mínimas de até 1550 kg/m³ e resistências à compressão superiores aos valores estipulados pela norma NBR NM 35 para as densidades apresentadas em todas as misturas / Abstract: With the discovery of admixtures and mineral additions many different types of concrete emerged over the last decades. But the own weight of conventional concrete is considered their biggest disadvantage. With this opens up the field for a material that despite being known to the Romans, it was little used, the concrete with lightweight aggregates. Much research and come in about two decades appears the self compacting concrete and more recently the lightweight concrete self compacting. This work proposes the study of this material still little explored concrete lightweight self compacting. For this are produced concrete with expanded clay in two different particle sizes: one coarse in total replacement of coarse aggregate of normal mass and a fine partially substituting fine aggregate. Are designed three families of concrete mixtures with different cement consumption, 320, 360 and 440 kg / m³ of concrete, and the tests carried out in the fresh state (ring J, V funnel and L box) and hardened (resistance to compression and traction , determining the modulus of elasticity, absorption, and density). The concretes were classified as self compacting and showed good results as to efficiency and resistance factor being possible to establish a correlation equations for its modulus of elasticity. For the density tests were observed concretes with minimum masses of up to 1550 kg / m³ and compressive strengths greater than those stipulated by NBR NM 35 standard for the densities presented in all mixtures / Mestrado / Tecnologia e Inovação / Mestre em Tecnologia
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/267741 |
Date | 28 August 2018 |
Creators | Verzegnassi, Emerson, 1968- |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Barbosa, Luísa Andréia Gachet, 1970-, Lintz, Rosa Cristina Cecche, 1971-, Trautwein, Leandro Mouta, Santos, Carlos Roberto dos |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Tecnologia, Programa de Pós-Graduação em Tecnologia |
Source Sets | IBICT Brazilian ETDs |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | 121 p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0718 seconds