Avaliação de propriedades físico-químicas de infiltrantes experimentais com adição de partículas de vidro bioativas = Evaluation of the physical-chemical properties of experimental infiltrants incorporated with bioactive glass particles / Evaluation of the physical-chemical properties of experimental infiltrants incorporated with bioactive glass particles

Orientador: Americo Bortolazzo Correr / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-27T03:22:53Z (GMT). No. of bitstreams: 1
Sfalcin_RavanaAngelini_D.pdf: 1513616 bytes, checksum: bd6dc4a4843283522343b56a58ef8ec7 (MD5)
Previous issue date: 2015 / Resumo: O objetivo neste trabalho foi avaliar as propriedades físico-químicas de infiltrantes resinosos com adição de partículas bioativas, bem como sua capacidade de penetração e dureza da profundidade em lesões subsuperficiais de esmalte. Uma blenda contendo TEGDMA (75% em peso) e BisEMA (25% em peso) foi manipulada e a partir dela foram incorporados 5 tipos de partículas bioativas (10% em peso): hidroxiapatita (HAp), fosfato de cálcio amorfo (ACP), vidro bioativo policarboxilato de zinco (BAG Zn), vidro bioativo 45S5 (BAG 45S5), cimento de silicato de cálcio modificado por ?-TCP (HCAT-?). Um material comercial foi utilizado (ICON®) como controle. Dez espécimes foram confeccionados para cada grupo de cada teste: rugosidade superficial (Ra) antes e após a escovação; Resistência à flexão por 3 pontos (RF) e módulo de elasticidade (ME); resistência coesiva à tração (RC); dureza Knoop (KHN); densidade de ligação cruzada (DLC); grau de conversão (GC); sorção (S) e solubilidade (SL) em água; e micro-dureza (KHN). Os dados foram submetidos a ANOVA e teste Tukey (?=0.05). A penetração dos infiltrantes resinosos no esmalte humano desmineralizado foi qualitativamente avaliada em Microscopia Confocal de Varredura a Laser (n=5). Os resultados mostraram que os menores valores de rugosidade (antes e após a escovação foram apresentados pelo ACP. Com relação à resistência a flexão e módulo de elasticidade, T+B apresentou o maior valor e ICON® mostrou o menor valor. ICON® também mostrou o menor valor de resistência coesiva à tração; não houve diferença significativa entre os grupos T+B, HAp, ACP, BAG Zn, BAG 45S5 e HCAT-?. Para o teste de dureza Knoop, ICON® obteve o menor valor e BAG Zn mostrou o maior valor. Para densidade de ligação cruzada, ICON® apresentou maior quantidade de ligação cruzada e HAp, menor quantidade de ligação cruzada. ICON® apresentou grau de conversão significantemente menor que os infiltrantes experimentais, que não diferiram entre eles. ICON® apresentou a maior sorção de água e HAp a menor. Não houve diferença significativa entre os demais grupos. Para solubilidade, ICON® apresentou os maiores valores, mas sem diferença de ACP. BAG 45S5 apresentou a menor solubilidade. Com relação a micro-dureza, não houve diferença estatisticamente significante entre as profundidades avaliadas (50 µm, 200 µm, 350 µm e 500 µm). BAG 45S5, BAG Zn e HCAT-? não mostraram diferença estatística entre eles. Entretanto, HCAT-? e BAG Zn foram similares ao ICON® e ACP. O grupo cariado mostrou menor valor quando comparado a todos os grupos testados. A análise em microscopia confocal mostrou que todos os materiais apresentaram boa capacidade de penetração nas lesões iniciais, exceto para FCA. Pôde ser concluído que adição de partículas bioativas em um infiltrante experimental melhorou as propriedades mecânicas e não afetou a capacidade de penetração dos infiltrantes. O infiltrante resinoso contendo fosfato de cálcio amorfo foi o que apresentou o melhor desempenho no teste de rugosidade de superfície antes e após a escovação / Abstract: The aim of this study was to evaluate the physical-chemical properties of the experimental infiltrants with the addition of bioactive particles as well as their capability of penetration and depth Knoop hardness into caries-like lesions. A control blend was made with TEGDMA (75 wt%) and BisEMA (25 wt%). Five bioactive fillers were added in the control blend (10 wt%): Hydroxyapatite (Hap), amorphous calcium phosphate (ACP), Zinc-polycarboxylated bioactive glass (BAG-Zn), bioactive glass 45S5 (BAG 45S5), and ?-TCP modified calcium silicate cements (HCAT-?). An available commercially material was used (ICON®). Ten specimens were comprised by each group for the following tests: Surface roughness (Ra) before and after brushing abrasion; flexural strength (FS) and elastic modulus (E-Modulus); tensile cohesive strength (TCS); Knoop hardness (KHN); softnening ratio (SR); degree of conversion (DC); water sorption (WS) and solubility (SL); and micro-hardness (micro-KHN). Data were subjected to ANOVA and Tukey¿s test (?=0.05). Confocal Scanning Laser Microscopy was used to evaluate qualitatively the penetration capability of resin infiltrants into demineralized human enamel. Results showed that ACP had the lowest Ra before and after brushing abrasion. Regarding to the FS and E-modulus, T+B showed the higher value and ICON® showed the lower value. Also, ICON® showed the lower value of TCS, but there was no significant statistically difference among the groups T+B, HAp, ACP, BAG Zn, BAG 45S5 e HCAT-?. To the KHN, ICON® obtained the lower value and BAG Zn showed the higher value. According to the SR, ICON® showed lower SR and HAp, the higher SR. ICON showed DC significantly lower than experimental resin infiltrants. Regarding to the WS, ICON® presented the highest water sorption and HAp the lowest one. There was no significant statistically difference among the other groups. ICON showed the highest SL results; however, the results were similar to ACP. The lowest SL was found for BAG 45S5. Regarding to the micro-KHN, there was no statistically difference among the analyzed depths (50 µm, 200 µm, 350 µm and 500 µm). BAG 45S5, BAG Zn and HCAT- ? did not show statistical difference among them. However, HCAT- ? and BAG Zn were similar to ICON® and ACP. Carious group showed lower value when compared to all the tested groups. Confocal microscopy analysis showed good capability of penetration into the initial lesions for all materials, except for ACP. It could be concluded that the addition of bioactive particles into an experimental infiltrant improved the mechanical properties and did not affect the capability of penetration into the experimental infiltrants. The resin infiltrant with amorphous calcium phosphate presented the best performance to the roughness surface before and after brushing abrasion / Doutorado / Materiais Dentarios / Doutora em Materiais Dentários

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288423
Date27 February 2016
CreatorsSfalcin, Ravana Angelini, 1985-
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Correr, Americo Bortolazzo, 1981-, Braga, Roberto Ruggiero, Borges, Alessandra Buhler, Pascon, Fernanda Miori, Consani, Simonides
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários
Source SetsIBICT Brazilian ETDs
LanguageMultilíngua
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis
Format64 f. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0023 seconds