Diploma thesis is focused on mechanical properties testing by small punch test and comparison of these properties with mechanical properties obtained by conventional tensile test. Steels P92 and AISI 316L in a shape of discs were tested. There were determined values of mechanical properties, namely yield stress, and ultimate tensile stress, obtained by the small punch test – constant deflection rate in this thesis. Values of initial stress and residual stress were evaluated from relaxation small punch test. Mechanical properties obtained by small punch test – constant deflection rate, and small punch test – relaxation, respectively, are compared with mechanical properties obtained by conventional tensile test, and relaxation tensile test, respectively. There were proposed own empirical relationships for restatement of mechanical properties obtained by small punch test to mechanical properties obtained by conventional tensile test in the thesis. Relatively small agreement of results obtained by small punch test, and conventional tensile test was demonstrated by a comparison. Application of own empirical relationships resulted in better agreement. Very good agreement of results of small punch test – relaxation, and relaxation tensile test was shown by their comparison.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:230952 |
| Date | January 2013 |
| Creators | Ječmínka, Marek |
| Contributors | Dobeš, Ferdinand, Dymáček, Petr |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0016 seconds