Utilization of methylaluminoxane (MAO) activated metallocene and constrained
geometry (CGC) olefin polymerization catalysts containing fluorenyl or
octamethyloctahydrodibenzofluorenyl (Oct) moieties has yielded three series of
syndiotactic copolymers of propylene with higher a-olefins. The melting temperatures
of these polymers were analyzed, and found to correspond directly with the mole percent
incorporation of comonomer, as well as with the frequency of stereoerrors in the
polymers. Further analysis indicated that rmrr stereoerrors, a result of site
epimerization, occur in close proximity to the incorporated comonomers.
The MAO-activated fluorenyl/Oct-containing metallocene and CGC catalysts were
further utilized to produce syndiotactic samples of poly(1-butene) (s-PB) and poly(1-
pentene) (s-PPe). The syndiotacticity of the samples was quantified by 13C NMR and
the melting temperatures determined by DSC. The samples of s-PB and s-PPe produced
by Me2Si( h1-C29H36)( h1-N-tBu)ZrCl2·OEt2 (Oct-CGC) were found to melt at higher
temperatures (55.9 and 43.1 °C, respectively) than any previously reported samples. The MAO-activated Oct-CGC was also used to produce polyethylene samples at a
variety of polymerization temperatures and pressures. All of the samples were found to
contain an unprecedented degree of branching (13-65 total branches per 1000 carbon
atoms) for an early transition metal single-site catalyst. The branches were found to be
almost exclusively of two or greater than five carbon atoms in length, and the levels of
the longer branches could be controlled by varying the polymerization conditions. The
number of ethyl branches was roughly 5 per 1000 carbon atoms for all samples.
Finally, a binary catalyst system comprising the Oct-CGC and a chromium-based
ethylene trimerization catalyst, ((tBuSCH2CH2)2NH)CrCl3, was developed. This MAOactivated
catalyst system could be tuned to produce polyethylene samples with 17-49
total branches per 1000 carbon atoms. Between 4 and 16 of these branches were found
to arise from incorporation of 1-hexene produced by the chromium oligomerization
catalyst. Adjusting the ratios of oligomerization catalyst, polymerization catalyst, and
activator was found to allow rational control over the branch content of the polymers.
The branching levels could also be varied by altering the time between injection of the
oligomerization and polymerization catalysts into the system.
| Identifer | oai:union.ndltd.org:tamu.edu/oai:repository.tamu.edu:1969.1/ETD-TAMU-2453 |
| Date | 15 May 2009 |
| Creators | Schwerdtfeger, Eric Dean |
| Contributors | Miller, Stephen A. |
| Source Sets | Texas A and M University |
| Language | en_US |
| Detected Language | English |
| Type | Book, Thesis, Electronic Dissertation, text |
| Format | electronic, application/pdf, born digital |
Page generated in 0.0018 seconds