The alumina-catalyzed Cope rearrangements of meso- and dl-3,4-diphenylhexa-1,5-diene were examined in detail, following up a preliminary observation by H. Berg at Portland State University. Commercial column-chromatography grade alumina was employed, and was further activated before use.by heating at 650-700° for four hours.
Using a ratio of 20 mg of dl-3,4-diphenylhex-l,5-diene to 1 g of alumina in heptane, the Cope rearrangement was complete within 15 minutes at room temperature to give exclusively trans,trans-1,6-diphenylhexa-1,5-diene. This was identified.by melting point, infrared spectroscopy and vapor phase chromatography
The catalyzed rearrangement of meso-3,4-diphenylhexa-l,5-diene was run using the same diene to alumina ratio. It was found that 31% of the meso-diene was converted to cis,trans- and trans,trans-l,6-diphenylhexa-1,5-diene at room temperature in four hours. Product iso-merization appeared to take place; the initial ratio of cis,trans-diene to trans,trans-diene was estimated to be 73:27. Another run was carried out at 60°, where the problem of isomerization of cis,trans-diene to trans,trans-diene was more pronounced. The rearrangement gave cis, trans-diene and trans,trans-diene in a ratio of 58:42, as estimated by extrapolation of the product ratio to zero time. Approximately 95% of meso-diene had reacted in one hour at this temperature. The extent of conversion of mes-diene was calculated by quantitative infrared spectroscopy, and the isomeric distribution of products was determined by vapor phase chromatography.
The product distribution in the alumina-catalyzed rearrangements parallels that of the thermal Cope rearrangement, where dl-diene gives exclusively trans,trans-diene at 80° with a half-life of eight hours and meso-diene gives 63% cis,trans-diene and 27% trans,trans-diene at 120° with a half-life of 15 hours.
| Identifer | oai:union.ndltd.org:pdx.edu/oai:pdxscholar.library.pdx.edu:open_access_etds-3409 |
| Date | 01 January 1974 |
| Creators | Wang, Paul Jhy-Shing |
| Publisher | PDXScholar |
| Source Sets | Portland State University |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Dissertations and Theses |
Page generated in 0.0019 seconds