Preparação de microesferas poliméricas à base de estireno, acetato de vinila e divinilbenzeno com propriedades magnéticas / Preparation of polymeric microsphereson styrene, vinyl acetate and divinybenzene with magnetic properties

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Microesferas poliméricas magnéticas à base de estireno (STY), divinilbenzeno (DVB), acetato de vinila (VAc) e ferro foram preparadas via polimerização em suspensão e semissuspensão. Foram estudadas as influências da concentração de VAc adicionado na polimerização e a presença de ferro sobre as características das partículas poliméricas obtidas. Estas partículas foram caracterizadas por espectrometria de absorção na região do infravermelho (FT-IR), análise térmica (TGA/DTA), microscopia óptica (MO), microscopia eletrônica de varredura (SEM) e magnetometria de amostra vibrante (VSM). Foram obtidas com sucesso microesferas poliméricas com propriedades magnéticas à base de estireno, divinilbenzeno e acetato de vinila. Estes materiais apresentaram bom controle morfológico, com maior rendimento na faixa de 120 a 75 m. Apresentaram também boas propriedades magnéticas (22,62 a 73,75 emu/g) com comportamento próximo de materiais superparamagnéticos e boa estabilidade térmica (444 C) / Magnetic polymeric microspheres based on styrene (STY), divinylbenzene (DVB), ethylene vinyl acetate (VAc) and iron were prepared via suspension and half suspension polymerization. The influence of the concentration of VAc and iron added to the polymerization on the characteristics of polymeric particles obtained were studied. These particles were characterized by infrared spectrometry (FT-IR), thermal analysis (TGA / DTA), optical microscopy (OM), scanning electron microscopy (SEM) and vibrating sample magnetometry (VSM). Polymeric microspheres with magnetic properties based on styrene, divinylbenzene and vinyl acetate were obtained. These materials showed good morphological control and large yield range from 120 to 75 micrometers. They also showed comparable magnetic properties (from 22.62 to 73.75 emu/g) to superparamagnetic materials and good thermal stability (444 C)

Identiferoai:union.ndltd.org:IBICT/urn:repox.ist.utl.pt:BDTD_UERJ:oai:www.bdtd.uerj.br:1510
Date24 March 2011
CreatorsJacira Aparecida Castanharo
ContributorsMarcos Antonio da Silva Costa, Ivana Lourenço de Mello, Marcia Cerqueira Delpech, Edwin Gonzalo Azero Rojas
PublisherUniversidade do Estado do Rio de Janeiro, Programa de Pós-Graduação em Química, UERJ, BR
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Formatapplication/pdf
Sourcereponame:Biblioteca Digital de Teses e Dissertações da UERJ, instname:Universidade do Estado do Rio de Janeiro, instacron:UERJ
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0026 seconds