The development of cottons with improved fiber quality has been a major objective in breeding programs around the world. Breeders have focused their attention on improving fiber strength and length, and have generally not used fiber elongation in the selection process. Although literature has reported a negative correlation between fiber elongation and tenacity, this correlation is weak and should not prevent breeders from simultaneously improving fiber tenacity and fiber elongation. Furthermore, the work of rupture property, important in the spinning process, could be best enhanced by improving both fiber tenacity and fiber elongation.
Fifteen populations were developed in 2007 by crossing good quality breeding lines with high elongation measurements to ‘FM 958’; a High Plains standard cultivar with good fiber quality but reduced elongation. Samples in every generation were ginned on a laboratory saw gin, and the lint was tested on HVI (High Volume Instrument). The F2 and F3 generations showed a wide range of variation for elongation (6.9% - 12.8% for the F2 and 4% - 9.20% for the F3) allowing divergent selection for low and high fiber elongation. A correlation (r) of -0.32 between strength and elongation was observed in the F2 individual plant selections. In the F3, the correlation (r) between strength and elongation was -0.36, and in the F4 the correlation (r) was -0.08. Nine lines were selected from the original 15 populations for spinning tests. The correlation between fiber elongation and strength for these lines was positive (r=0.424), indicating that with targeted selection, fiber elongation and strength can be simultaneously improved.
Fiber elongation was positively correlated with yarn tensile properties tenacity (r=0.11), work-to-break (r=0.68) and breaking elongation (r=0.87); and was negatively correlated with yarn evenness properties, number of thin places (r=-0.16), number of thick places (r=-0.9), nep count (r=-0.24), hairiness (r=-0.38) and total number of imperfections (r=-0.38). All selections for high elongation were superior for all tensile properties compared to the low selections and the check in the analysis over locations and in each location. Furthermore, selections for high elongation were significantly different from the selections for low elongation and the check.
In addition to developing lines for fiber spinning tests with improved, or differentiated, fiber elongation, this project was amended to evaluate and determine the heritability of fiber elongation. Three different methodologies were used to obtain estimates of heritability; variance components, parent off-spring regression, and realized heritability using F3, F4, and F5 generation. No inbreeding was assumed because there was no family structure in the generations within this study. Estimates of heritability by the variance component methods in the F3, F4 and F5 were 69.5%, 56.75% and 47.9% respectively; indicating that 40-50% of the variation was due to non-genetic effects. Parent off-spring regression estimates of heritability were 66.1% for the F3-4 and 62.8% for the F4-5; indicating a high resemblance from parents to off-spring. Estimates of realized heritability were obtained to determine the progress realized from selection for the low and high selection for fiber elongation. Estimates were intermediate (0.44–0.55), indicating moderately good progress from selection.
The results from this project demonstrate that it is possible to improve fiber elongation and to break the negative correlation between elongation and strength. Furthermore, it has been demonstrated that improving fiber elongation results in the increase of length uniformity index and decreased short fiber content. Additionally, directed divergent selection was a successful methodology for the improvement of fiber elongation, and was useful to demonstrate that higher fiber elongation has a positive effect on yarn tensile properties, yarn evenness and processing. The development of new cultivars with improved fiber elongation will improve the quality and reputation of U. S.-grown cotton. The ultimate result will be better yarn quality and improved weaving efficiency, and particularly address current weaknesses in U. S. –grown cotton cultivars, especially from the High Plains of Texas, of more short fiber content, lower uniformity ratios, and weaker yarn strength.
| Identifer | oai:union.ndltd.org:tamu.edu/oai:repository.tamu.edu:1969.1/148196 |
| Date | 14 March 2013 |
| Creators | Osorio Marin, Juliana 1982- |
| Contributors | Hague, Steve, Dever, Jane K |
| Source Sets | Texas A and M University |
| Detected Language | English |
| Type | Thesis, text |
| Format | application/pdf |
Page generated in 0.0021 seconds