A simulation model which incorporates the statistical- and numerical-based Lattice Green Function Local Load Sharing Model and a Fracture Mechanics-based Residual Strength Model has been developed. The model simulates creep rupture by imposing a fixed load of constant stress on the composite over the simulation duration. Simulation of the fatigue of glass fiber-reinforced composites is achieved by replacing the constant stress parameter in the model with a sinusoidal wave function. Results from the creep rupture model using fused silica fiber parameters, compare well with S-2 glass/epoxy systems. Results using Mandell's postulate that fatigue failure in glass fiber-reinforced polymeric composites is a fiber-dominated mechanism, with a characteristic slope of 10 %UTS/decade are consistent with available experimental data. The slopes of fatigue curves for simulated composites for three frequencies namely: 2, 5 and 10 Hz are within 12-14 %UTS/decade compared with that of 10.6-13.0%UTS/decade for unidirectionl glass reinforced composites (epoxy and vinyl ester) obtained from Demers' [40] data. / Master of Science
Identifer | oai:union.ndltd.org:VTETD/oai:vtechworks.lib.vt.edu:10919/36924 |
Date | 21 August 1998 |
Creators | McBagonluri-Nuuri, David Fred |
Contributors | Engineering Science and Mechanics, Lesko, John J., Dillard, David A., Gao, David Y., Case, Scott W. |
Publisher | Virginia Tech |
Source Sets | Virginia Tech Theses and Dissertation |
Detected Language | English |
Type | Thesis |
Format | application/pdf |
Rights | In Copyright, http://rightsstatements.org/vocab/InC/1.0/ |
Relation | Thesis.pdf |
Page generated in 0.002 seconds