Crosslinkable mixed matrix membranes for the purification of natural gas

Mixed matrix nanocomposite membranes composed of a crosslinkable polyimide matrix and high-silica molecular sieve particles were developed for purifying natural gas. It was shown that ideal mixed matrix effects were not possible without sieve surface modification. A previously developed Grignard procedure was utilized to deposit magnesium hydroxide nanostructures on the sieve surface in order to enhance polymer adhesion. Analyses of Grignard-treated sieves pointed to the formation of non-selective voids within the surface deposited layer. These voids were suspected to lead to lower-than-expected membrane performance. In order to improve membrane transport, a reactive sizing procedure was developed to fill these voids with polyimide-miscible material. In a serendipitous discovery, as-received sieves--when treated with this reactive sizing procedure--resulted in nearly identical membrane performance as reactive-sized, Grignard-treated sieves. This observation lead to the speculation of a non-ideal transport mechanism in mixed matrix membranes.

Identiferoai:union.ndltd.org:GATECH/oai:smartech.gatech.edu:1853/39465
Date11 January 2010
CreatorsWard, Jason Keith
PublisherGeorgia Institute of Technology
Source SetsGeorgia Tech Electronic Thesis and Dissertation Archive
Detected LanguageEnglish
TypeDissertation

Page generated in 0.0016 seconds