Yttria stabilized zirconia (YSZ) is the state of the art ceramic top coat material used for TBC applications. The desire to achieve a higher engine efficiency of agas turbine engine by increasing the turbine inlet temperature has pushed YSZ toits upper limit. Above 1200°C, issues such as poor phase stability, high sinteringrates, and susceptibility to CMAS (calcium magnesium alumino silicates) degradation have been reported for YSZ based TBCs. Among the new materials,gadolinium zirconate (GZ) is an interesting alternative since it has shown attractive properties including resistance to CMAS attack. However, GZ has a poor thermo-chemical compatibility with the thermally grown oxide leading to poor thermal cyclic performance of GZ TBCs and that is why a multi-layered coating design seems feasible.This work presents a new approach of depositing GZ/YSZ multi-layered TBCs by the suspension plasma spray (SPS) process. Single layer YSZ TBCs were also deposited by SPS and used as a reference.The primary aim of the work was to compare the thermal conductivity and thermal cyclic life of the two coating designs. Thermal diffusivity of the YSZ single layer and GZ based multi-layered TBCs was measured using laser flash analysis (LFA). Thermal cyclic life of as sprayed coatings was evaluated at 1100°C, 1200°C and 1300°C respectively. It was shown that GZ based multi-layered TBCs had a lower thermal conductivity and higher thermal cyclic life compared to the single layer YSZ at all test temperatures. The second aim was to investigate the isothermal oxidation behaviour and erosion resistance of the two coating designs. The as sprayed TBCs were subjected toisothermal oxidation test at 1150°C. The GZ based multi-layered TBCs showed a lower weight gain than the single layer YSZ TBC. However, in the erosion test,the GZ based TBCs showed lower erosion resistance compared to the YSZ singlelayer TBC. In this work, it was shown that SPS is a promising production technique and that GZ is a promising material for TBCs.
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:hv-9854 |
| Date | January 2016 |
| Creators | Mahade, Satyapal |
| Publisher | Högskolan Väst, Avdelningen för avverkande och additativa tillverkningsprocesser (AAT), Trollhättan : University West |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Licentiate thesis, comprehensive summary, info:eu-repo/semantics/masterThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | Licentiate Thesis : University West ; 11 |