Introduction: Embolic agents are used to block blood flow of hypervascular tumours, ultimately resulting in target tissue necrosis. However, this therapy is limited by the formation of new blood vessels within the tumour, a process known as angiogenesis. Targeting angiogenesis led to the discovery of anti-angiogenic factors, large molecular weight proteins that can block the angiogenic process. The aim of this research is development of poly (vinyl alcohol) (PVA) aqueous solutions that cross-link in situ to form a hydrogel that functions as an embolic agent for delivery of macromolecular drugs. Methods: PVA (14 kDa, 83% hydrolysed), functionalised by 7 acrylamide groups per chain, was used to prepare 10, 15, and 20wt% non-degradable hydrogels, cured by UV or redox initiation. Structural properties were characterised and the release of FITCDextran (20kDa) was quantified. Degradable networks were then prepared by attaching to PVA (83% and 98 % hydrolysed) ester linkages with an acrylate end group. The effect on degradation profiles was assessed by varying parameters such as macromer concentration, cross-linking density, polymer backbone and curing method. To further enhance the technology, radiopaque degradable PVA was synthesised, and degradation profiles were determined. Cell growth inhibition of modified PVA and degradable products were also investigated. Results: Redox initiation resulted in non-degradable PVA networks of well-controlled structural properties. Increasing the solid content from 10 to 20wt% prolonged the release time from few hours to ~ 2 days but had no effect on the percent release, with only a maximum release of 65% achieved. Ester attachment to the PVA allowed flexibility in designing networks of variable swelling behaviors and degradation times allowing ease of tailoring for specific clinical requirements. Synthesis of radiopaque degradable PVA hydrogels was successful without affecting the polymer solubility in water or its ability to polymerize by redox. This suggested that this novel hydrogel is a potential liquid embolic with enhanced X-ray visibility. Degradable products had negligible cytotoxicity. Conclusion: Novel non-degradable and radiopaque degradable PVA hydrogels cured by redox initiation were developed in this research. The developed PVA hydrogels showed characteristics in vitro that are desirable for the in vivo application as release systems for anti-angiogenic factors.
Identifer | oai:union.ndltd.org:ADTP/281267 |
Date | January 2005 |
Creators | Mawad, Damia, Graduate School of Biomedical Engineering, Faculty of Engineering, UNSW |
Publisher | Awarded by:University of New South Wales. Graduate School of Biomedical Engineering |
Source Sets | Australiasian Digital Theses Program |
Language | English |
Detected Language | English |
Rights | Copyright Damia Mawad, http://unsworks.unsw.edu.au/copyright |
Page generated in 0.139 seconds