Previous issue date: 2010-07 / Nenhuma / Grande parte das pesquisas com agregados provenientes da britagem de resíduos de construção e demolição (RCD) tem como foco principal o comportamento mecânico de concretos compostos com estes agregados. Este trabalho tem por objetivo o estudo das propriedades de concretos com agregados reciclados de concreto (ARC), abordando além das propriedades mecânicas de resistência à compressão e tração, questões relacionadas à durabilidade com ênfase na carbonatação. Para controlar as características do concreto reciclado, estes foram produzidos em laboratório com as seguintes resistências 18, 37 e 50 MPa, com o intuito de resultar em três agregados com porosidades distintas. Após 63 dias de cura submersa, este concreto foi britado e empregado como substituição parcial do agregado natural (AN) em um novo concreto que, por sua vez, foi moldado com uma relação água/aglomerante de 0,64. O ARC foi empregado em substituição ao AN em diversos teores (0, 25, 50, 75 e 100%). Previamente ao emprego, o ARC foi pré-molhado com teores de 0, 25, 50, 75 e 100% da água relativa à absorção total do resíduo. Para a verificação da durabilidade deste novo concreto quando exposto ao CO2, empregou-se o ensaio acelerado de carbonatação, realizado em câmara de alimentação contínua com atmosfera de 1% de concentração de CO2 e umidade relativa de 70% ± 5%, na qual os concretos permaneceram durante 147 dias. Os resultados obtidos a partir da leitura da profundidade carbonatada nas idades estudadas apresentam um comportamento semelhante tanto para os concretos de referência, quanto para os concretos que incorporam ARC. Somente para concretos que incorporam um alto percentual de substituição nota-se um ligeiro aumento da profundidade de carbonatação em relação aos concretos de referência. Com base nestes resultados pode-se inferir que até um percentual de 50% de substituição do AN por ARC com qualquer teor de pré-molhagem, a profundidade de carbonatação observada é a mesma para concretos com ARC e concretos de referência. / Much of the research with aggregates from crushing of construction and demolition waste (CDW) has focused primarily on the mechanical behavior of concrete made with these aggregates. This research aims at to study the properties of concrete made with recycled concrete aggregates (RCA), besides addressing the mechanical properties, the durability issues will be focused on the carbonation. To control the characteristics of recycled aggregate, they were produced in the laboratory with the water/cement ratios: 0,85, 0,56 and 0,43, in order to result in three types of aggregates with different porosities. After 63 days of curing under water, the concrete was crushed and used as partial replacement of natural aggregate (NA) in a new concrete which was made with a water/cement ratio of 0,64. The RCA was used to replace the NA at various levels of 0, 25, 50, 75 and 100%. Prior to employ the RCA, it has been pre-wetted with levels of 0, 25, 50, 75 and 100% of water absorption on the total residue. To check the durability of the new concrete when exposed to CO2, the accelerated carbonation test was carried out, performed in a climatic chamber with a constant atmosphere of 1% CO2 and relative humidity of 70% ± 5%, in which the concrete remains for 147 days. The results reading from the carbonation depth at the ages 1, 3, 7, 28, 63, 91 and 147 days, show a similar behavior for both, concrete reference and concrete with RCA. Only concrete that incorporate a high percentage of replacement shows an increase in carbonation depth in relation to the reference concrete. Based on the results it is possible to infer that at replacements of NA to RCA lower than 50%, for any content of pre-wetting, the carbonation depth observed is the same for reference concrete and concrete with RCA.
| Identifer | oai:union.ndltd.org:IBICT/oai:www.repositorio.jesuita.org.br:UNISINOS/3616 |
| Date | 27 July 2010 |
| Creators | Werle, Ana Paula |
| Contributors | http://lattes.cnpq.br/8647433523617676, Kulakowski, Marlova Piva, Kazmierczak, Claudio de Souza |
| Publisher | Universidade do Vale do Rio dos Sinos, Programa de Pós-Graduação em Engenharia Civil, Unisinos, Brasil, Escola Politécnica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UNISINOS, instname:Universidade do Vale do Rio dos Sinos, instacron:UNISINOS |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0021 seconds