Orientador : Simonides Consani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-02T13:58:39Z (GMT). No. of bitstreams: 1
Chaves_Eclerion_D.pdf: 2686935 bytes, checksum: a0aae1903153a990c6baf47e2d25878c (MD5)
Previous issue date: 2002 / Resumo: O objetivo deste estudo foi avaliar o efeito do tempo de armazenagem inicial na resistência à tração de três cimentos resinosos unidos à dentina. Foram utilizados 120 dentes bovinos. Os dentes foram embutidos, desgastados com lixas de granulação 220 e 600 e limpos em ultra-som. A seguir foram divididos em 3 grupos contendo 20 amostras: Grupo I foi usado o Cimento Rely X; Grupo II, Cimento Enforce e Grupo III, Cimento Dual Cement. As amostras de cada grupo foram cimentadas com os materiais preparados de acordo com as instruções de cada fabricante. A seguir, os dentes foram embutidos aos pares e posicionados em uma matriz, com as superfícies tratadas em contato entre si para o procedimento de fixação com o cimento resinoso. A resina foi fotopolimerizada por 160 segundos e os corpos-de-prova armazenados a 37° C e 100% de umidade relativa. A seguir, com o auxílio de uma matriz metálica, os corpos-de-prova foram submetidos ao ensaio de tração em uma máquina de ensaio universal INSTRON (modelo 4411) a velocidade de 1 mm/min. Metade das corpos-de-prova foram tracionadas após 30 minutos e a outra metade após 24 horas. Os resultados obtidos foram submetidos à análise de variância e ao teste de Tukey (p<0,05%). As médias obtidas foram as seguintes: Grupo I, 30 minutos = 2,53 (+0,49) MPa; 24 horas = 2,90 (+1, 12) MPa; Grupo II, 30 minutos = 1,65 (+0,46) MPa, 24 horas = 1,94 (+0,43) MPa; Grupo III, 30 minutos = 4,24 (+1,26) MPa; 24 horas = 6,14 (+01,80) MPa. Após o ensaio de resistência à tração, as superfícies fraturadas e representativas dos corpos-de-prova foram analisadas sob microscopia eletrônica de varredura para determinar o predomínio do padrão de fratura na interface. Tendo por base os resultados obtidos e discutidos na pesquisa podemos concluir que Os valores médios de resistência à tração, para os grupos I e II, obtidos a partir de corpos-de-prova tracionados nos períodos de 30 minutos não diferiram estatisticamente (p<0,05) dos tracionados em 24 horas, com exceção do grupo III que apresentou diferença estatística. Os valores médios de resistência á tração obtidos individualmente para os grupos I (Re/y X), grupo II (Enforce) e III (Dua/ Cement) apresentaram diferenças estatísticas significantes entre si (P<0,05). Comparando-se os tempos e os valores obtidos, verifica-se uma proporcionalidade direta entre o tempo e a resistência, o que implica em um tempo maior para que o processo de polimerização ocorra de forma satisfatória / Abstract: The objective of this study was to evaluate the effect of the initial storage time in tensile strength of three resin cements bonded to dentin. Sixty bovine teeth were used. The teeth were embedded, polished with silicon carbide papers of 220 and 600 grit and cleaned on ultra-sonic. They were divided in 3 groups of 20 samples each: Group I was fixed with Rely X cement; Group II, Enforce and Group III, Dual Cement. The samples of each group were lutted with the above materials according to each manufacturer's instructions. Half of the samples were tested after 30 minutes, and the other half, after 24 hours. The teeth were embedded to the pairs and positioned in adie stamp, with the surfaces face-to-face to each other and in contact for the adhesive procedure with the resin cement. The resin was photocured for 160 seconds and each specimen was them stored for 30 minutes or 24 hours at 37° C and 100% of relative humidity. With the aid of a metallic die stamp the samples were submitted to the tensile test in machine of universal test INSTRON I (model 4411) at speed of 1 mm/min. The results were submitted to the variance analysis and to Tukey's test (5%). The obtained averages were the following (SD): Group I, 30 minutes = 2,53 (+0,49) MPa; 24 hours = 2,90 (+1,12) MPa; Group II, 30 minutes = 1,65 (+0,46) MPa, 24 hours = 1,94 (+0,43) MPa; Group III, 30 minutes = 4,24 (+1,26) MPa; 24 hours = 6,14 (+01,80) MPa. After the tensile strength test, the surfaces of one of the tested samples were analyzed under SEM in order to determine the prevalence of the fracture pattern in the interface. Based upon the results obtained and discussed on this study can conclude that the mean values of tensile strength for groups I and groups II Obtained with the samples tested on the period of 30 mino did not differ statistically from those tested 24 h., except for group III that differ statistically. The Mean values of tensile strength of groups I, II e III were statistically different among them. Comparing time and values obtained, it is possible to verify a direct proportionality between time and strength, what means that a longer time is necessary to allow the polymerization process to occur in a satisfactory way / Doutorado / Materiais Dentarios / Doutor em Odontologia
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/290113 |
| Date | 25 October 2002 |
| Creators | Chaves, Eclerion |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Consani, Simonides, 1939-, Cruz, Carlos Alberto dos Santos, Oshima, Hugo Mitsuo Silva, Correr Sobrinho, Lourenço, Sinhoreti, Mário Alexandre Coelho |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 88f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.002 seconds