Orientador: Regina Maria Puppin-Rontani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T06:00:37Z (GMT). No. of bitstreams: 1
Correr-Nolasco_GiseleMaria_M.pdf: 5607867 bytes, checksum: bb98da2fe571d84a31f2c91744a11f0a (MD5)
Previous issue date: 2003 / Resumo: O objetivo deste estudo foi avaliar diferentes sistemas de união (Single Bond - SB, Prime & Bond 2.1 - PB e Clearfil SE Bond - CSEB), aplicados à dentina de dentes decíduos, submetida ou não ao tratamento prévio com
hipoclorito de sódio (NaDCI), através da análise da resistência da união ao cisalhamento (RC) e do aspecto morfológico da união compósito/dentina. Foram selecionados 45 molares decíduos hígidos extraídos. As raízes dos dentes foram
seccionadas na junção cemento-esmalte e as coroas ao meio, no sentido mésiodistal. As amostras foram então embutidas com resina de poliestireno em tubos de PV.C., com a superfície vestibular, lingual ou palatina externamente e lixadas até
a obtenção de uma superfície plana em dentina (3 mm de diâmetro). A seguir, foram aleatoriamente distribuídas em 6 grupos (n=15), sendo: G1 - aplicação do sistema SB; G2 - condicionamento ácido (CA), aplicação de NaOCI seguida pelo
sistema SB; G3 - aplicação do sistema PB; G4 - CA, aplicação do NaOCI seguida pelo sistema PB; G5 - aplicação do sistema CSEB e G6 - aplicação de NaOCI, seguida pelo CSEB. Todos os sistemas de união foram aplicados de acordo com
as instruções dos fabricantes. O NaOCI a 10%foi aplicado nos grupos 2,4 (após o condicionamento ácido) e 6 (antes da aplicação do sistema de união) por 60s, e o dente foi lavado por 30s e seco com papel absorvente. Em seguida, o compósito
Filtek Z-250 foi inserido em três incrementos (aproximadamente 2 mm), em uma matriz bipartida de silicone por adição adaptada a um posicionador metálico, e fotoativado por 20s cada incremento. As amostras foram armazenadas em água
destilada a 37°C por 24h e então submetidas ao ensaio de cisalhamento em uma Máquina de Ensaio Universal (Instron - modelo 4411) à velocidade de 0,5mm/min. Os padrões de fratura foram observados em microscópio estereoscópico (aumento 25X), e os representativos de cada grupo foram observados em Microscopia Eletrônica de Varredura (MEV). Para a análise da união compósito/dentina foram utilizados três dentes para cada grupo e repetidos todos os procedimentos
descritos anteriormente. Emseguida, foram seccionados no centro da restauração e preparados para observação em MEV. Os dados obtidos no ensaio de cisalhamento foram submetidos à análise de variância e teste de Tukey (p<0,05).
Os valores obtidos em MPa foram: G1- 3,17 :t 1,97; G2 - 2,93 :t 1,36; G3 - 2,04 :t 0,27; G4 - 1,91 :t 0,74; G5 - 2,67 :t 1,22; G6 -2,14 :t 1,10. De acordo com os resultados, pôde-se observar que houve diferença estatística significativa (p<0,05)
entre os materiais (SB-CSEB-PB). Não houve diferença estatística significativa entre os grupos com ou sem tratamento do substrato, independente do material utilizado (p>0,05). O tipo de falha freqüentemente observada em todos os grupos
foi a falha mista (coesiva no compósito + adesiva). Com relação ao aspecto . morfológico da união, nas amostras sem tratamento do substrato foi observada a presença da camada híbrida e dos prolongamentos resinosos. Nas amostras com
tratamento da superfície (com NaOCI) não foi observada a presença da camada híbrida, porém foram observados prolongamentos resinosos. Pôde-se concluir que o tratamento da superfície com hipoclorito de sódio não afetou a resistência da união compósito/dentina ao cisalhamento, porém, interferiu na formação da camada híbrida, em dentes decíduos / Abstract: The aim of this study was to evaluate different bonding agents (Single Bond - SB, Prime & Bond 2.1 - PB e Clearfil SE Bond - CSEB), in primary teeth treated with sodium hypochlorite (NaOCI) on the shear bond strength (SBS) and
micromorphology of the resin/dentin interface. Forty-five sound extracted primary molars were selected. The roots were sectioned in the enamel-cement junction and the crowns longitudinally, in the mesio-distal sense. The samples were embedded in polystyrene resin with the bucal, lingual or palatine surface externally and they were flattened until dentin surface was reached (3mm in diameter). Then, the samples were randomly assigned in 6 groups (n=15), and received the following
treatments: G1 - SB; G2 - acid etching (AE), 10% NaOCI and the SB; G3 - PB; G4 - AE, 10% NaOCI and the PB; G5 - CSEB; G6 - 10% NaOCI followed by CSEB. Ali the adhesive systems were applied according to manufactures' instructions. The 10% NaOCI solution was applied for 60s in groups 2,4 (after acid etching), and 6 (before adhesive system), washed for 30s and dried with tissue paper. Next, the composite resin was inserted in increments (2mm) in a vinyl polysiloxane impression material matrix, adapted in a metallic holder, and light cured for 20s (each increment). The samples were stored in distilled water at 37°C
for 24h and then, submitted to SBS test in a universal testing machine (Instron - model 4411) with a crosshead speed of 0.5mm/min. The failure sites were observed in stereoscope microscopy of 40X magnification, and the representative
failures of each group were observed in Scanning Electron Microscopy (SEM). The results obtained were submitted to ANOVA and Tukey's tests (p<0.05). The values in MPa were: G1- 3.17 :t 1.97;G2 - 2.93:t 1.36;G3 - 2.04:t 0.27; G4- 1.91 :t
0.74; G5 - 2.67:t 1.2; G6 -2.4:t 1.0. According to the results, it could be noticed that there was a statistical significant difference (p<0.05) among the materiais (SB- CSEB PB). There was no statistical significant difference (p>0.05) among ali
the groups with or without treatment of the substrate, independently of the material used. The mixed fail (cohesive in resin + adhesive) was the one most frequently observed in ali groups. Regarding the interface aspect in specimens without
substrate treatment (NaDCI) it could be observed the presence of the hybrid layer and resin tags whereas treated specimens only resin tags could be observed. It could be concluded that the treatment of the dentin surface with sodium
hypochlorite did not affect the resin/dentin bonding strength but interfered in the hybrid layer formation in primary teeth / Mestrado / Mestre em Materiais Dentários
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288619 |
Date | 31 March 2003 |
Creators | Correr-Nolasco, Gisele Maria |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Puppin-Rontani, Regina Maria, 1959-, Rodrigues, Celia Regina Martins Delgado, Sinhoreti, Mário Alexandre Coelho |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | 161p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0025 seconds