Submitted in fulfilment of the degree of Doctor of Dental Material Science in the
Department of Dental Services,
Faculty of Health Sciences,
Durban University of Technology,
Durban, South Africa, 2008. / Introduction: Incorporating a feldspar chemical bond between alumina filler particles is expected to increase the wear resistant and flexural strength properties, while reducing flexibility of dental composites. Aims and Objectives: An investigation was carried out to evaluate the influence of the feldspar chemical bonding between alumina filler particles on wear, flexural strength and flexibility of experimental alumina/feldspar dental composites. It was hypothesized that wear resistance and flexural strength would be significantly increased with increased feldspar mass, while flexibility was expected to decrease. Methods: Alumina was chemically sintered and bonded with 30%, 40%, 50% and 60% feldspar mass, silanized and infiltrated with UDMA resin to prepare the dental restorative composite material specimens. Results and conclusions: Significantly higher wear resistant characteristics resulted with increased feldspar mass (p<0.5). Improvements in flexural strength characteristics as the feldspar mass was increased was not statistically different (p>0.5). Flexibility characteristics as the feldspar mass was increased was not statistically different (p>0.5). The alumina/feldspar specimens showed lower flexibility (mm displacement) than SR ADORO (p<0.05). Feldspar chemical bonding between the alumina particles may improve on the wear resistance and Flexibility of alumina/feldspar composites when compared to SR ADORO. This study evaluated the influence of a chemical feldspar bond between alumina filler particles.
Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:dut/oai:ir.dut.ac.za:10321/430 |
Date | January 2008 |
Creators | Le Roux, Andre Rayne |
Contributors | Lachman, Nirusha, Walker, Mark, Botha, C. Theo |
Source Sets | South African National ETD Portal |
Language | English |
Detected Language | English |
Type | Thesis |
Page generated in 0.002 seconds