A thorough study on the distribution of defect-related active energy levels has been performed on nanocrystalline TiO2. Films have been deposited on thick-alumina printed circuit boards equipped with electrical contacts, heater and temperature sensors, to carry out a detailed thermally stimulated currents analysis on a wide temperature range (5-630 K), in view to evidence contributions from shallow to deep energy levels within the gap. Data have been processed by numerically modelling electrical transport. The model considers both free and hopping contribution to conduction, a density of states characterized by an exponential tail of localized states below the conduction band and the convolution of standard Thermally Stimulated Currents (TSC) emissions with gaussian distributions to take into account the variability in energy due to local perturbations in the highly disordered network. Results show that in the low temperature range, up to 200 K, hopping within the exponential band tail represents the main contribution to electrical conduction. Above room temperature, electrical conduction is dominated by free carriers contribution and by emissions from deep energy levels, with a defect density ranging within 10(14)-10(18) cm(-3), associated with physio- and chemi-sorbed water vapour, OH groups and to oxygen vacancies.
| Identifer | oai:union.ndltd.org:arizona.edu/oai:arizona.openrepository.com:10150/627084 |
| Date | 05 January 2018 |
| Creators | Bruzzi, Mara, Mori, Riccardo, Baldi, Andrea, Carnevale, Ennio, Cavallaro, Alessandro, Scaringella, Monica |
| Contributors | Univ Arizona, LBT Observ |
| Publisher | MDPI AG |
| Source Sets | University of Arizona |
| Language | English |
| Detected Language | English |
| Type | Article |
| Rights | © 2018 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution (CC BY) license. |
| Relation | http://www.mdpi.com/2079-4991/8/1/13 |
Page generated in 0.0021 seconds