Heterogeneous welded joints – type ferrite/austenite is inseparable part of structure for energy industry. Welding conditions and post weld heat treatment have a significant impact on the structural stability of welded joint. The structure determines resulting mechanical properties that determine lifetime of these joints. At the same time in microstructure changes in heat affected zone of the base material is diffusion of carbon through the weld interface. This work is focused on the analysis of structural stability of heterogeneous weld carbon/austenitic steel, which was formed carbon steel 22K (base material) and austenitic buttering layer EA 395/9 with a higher content of nickel. Evaluation of the structure was focused on the structure of weld metal (Böhler FOX SAS 2) and structure of the heat affected zone of base material. Metallographic evaluation was performed on the light microscope and scanning electron microscope equipped with the energy and wave dispersive analysis, which identified the contents of substitutional elements and carbon on the interface of carbon/austenitic steel. The results of metallographic analysis were compared with measurements of Vickers hardness and microhardness and calculations using Thermo-Calc software and software SVARY. The description and evaluation of the stability of the weld joints was determined by carbon content of the course interface using wave dispersive spectroscopy. The results of energy dispersive analysis were used to determine the type of carbides present at the interface of carbon/austenitic steel.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:230237 |
| Date | January 2012 |
| Creators | Havlík, Petr |
| Contributors | Stránský, Karel, Foret, Rudolf |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0059 seconds