In this study, a series of denim fiberboards are fabricated using two different resins, malamine urea formaldehyde (MUF) and polymeric methylene diphenyl diisocyanate (pMDI). Two experimental design factors (1) adhesive content and (2) MUF-pMDI weight ratio, were studied. All the denim fiberboard samples were fabricated following the same resin blending, cold-press and hot-press procedures. The physical and mechanical tests were conducted on the fiberboard following the procedures described in ASTM D1037 to obtain such as modulus of elasticity (MOE), modulus of rupture (MOR), internal bond (IB), thickness swell (TS), and water absorption (WA). The results indicated that the MOE was significantly affected by both factors. IB was affected significantly by weight ratio of different glue types, with 17 wt% more MDI resin portion in the core layer of the denim boards, the IB for total adhesive content 15% fiberboard was enhanced by 306%, while for total adhesive content 25% fiberboard, enhanced by 205%. TS and WA, with higher adhesive content used in denim boards' fabrication, and more pMDI portion in the core layer of the boards, the boards' TS and WA was reduced by up to 64.2% and 78.8%, respectively.
| Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc1505281 |
| Date | 05 1900 |
| Creators | Cui, Zhiying |
| Contributors | Shi, Sheldon, Zhang, Haifeng, Zhao, Weihuan |
| Publisher | University of North Texas |
| Source Sets | University of North Texas |
| Language | English |
| Detected Language | English |
| Type | Thesis or Dissertation |
| Format | vii, 47 pages, Text |
| Rights | Public, Cui, Zhiying, Copyright, Copyright is held by the author, unless otherwise noted. All rights Reserved. |
Page generated in 0.0016 seconds