Previous issue date: 2001-10-19 / CNPq / O setor de revestimentos cerâmicos vem apresentando elevados índices de crescimento
nos últimos anos, o que consolida a posição do Brasil como um dos maiores produtores
mundiais, bem como grande exportador em potencial. Todavia esse crescimento veio
acompanhado por uma exigência crescente de melhor qualidade, fazendo-se necessário, cada dia mais pesquisas sobre revestimentos cerâmicos. Assim esse trabalho tem por fim estudar a expansão por umidade e as características cerâmicas correlatas (absorção de água, resistência ao gretamento e expansão térmica) de pisos cerâmicos frente a normalização da ABNT, bem como procurar determinar inter-relações entre essas propriedades. Foi feita a aquisição de vinte e três amostras de dezenove marcas de revestimentos cerâmicos vendidas no comércio de Campina Grande - PB, oriundas de estados do sudeste e nordeste. Em seguida foram realizados ensaios de determinação de absorção de água, coeficiente de dilatação térmica, resistência ao gretamento e expansão por umidade, todos de acordo com a norma NBR 13818. Com base nos resultados obtidos pode-se concluir que: a grande maioria dos revestimentos estudados situa-se na classe dos materiais semi-porosos, com absorção de água entre 6-10%; cerca de 30% dos revestimentos apresentaram trincas após o ensaio de resistência ao gretamento; que a maioria dos revestimentos tiveram EPU após fervura entre 0,01 e 0,03%, sendo indicado na norma NBR 13818 que expansões acima de 0,06% podem contribuir para
problemas nos revestimentos; a fervura aparenta provocar uma lixiviação dos corpos de prova durante o ensaio de determinação da EPU; a análise utilizado diagramas de fase indicou que os revestimentos estudados apresentam uma relação decrescente entre a absorção de água e a quantidade estimada de fase vítrea, bem como um comportamento crescente entre a EPU, após fervura, e a quantidade estimada de fase vítrea e que os valores obtidos para os coeficientes de dilatação térmica linear situaram-se no intervalo de 6 a 8 xlO"6 °C , sendo indicado na norma EN 103 valores inferiores a 9 xlO"6 °C'\ quando os revestimentos cerâmicos são processados por prensagem. / The ceramic tile sector has showing high increasing indexes in the last years, what
ratify the position of Brazil as one of the principal world producer and great exporter, in
potential. Although this increasing came with a raised demand by better quality, making
necessary more research on ceramic tiles. Thus, this work has as aim study the moisture
expansion and correlated ceramic characteristics (water absorption, crazing-resistance and thermal expansion) of ceramic tiles, according the ABNT standardization, and try to
determine inter-relations between these properties. Were bought twenty tree samples of
nineteen commercial brands of ceramic tiles in the market of Campina Grande - PB that are originated from plants of the northeastern and southeastern states. Afterwards were did tests to determine the water absorption, thermal expansion, crazing-resistance and moisture expansion, all of them according to the NBR 13818 norm. Based in the results can be concluded that: the great majority of the ceramic tiles studied were in the class of the semiporous materials, with absorption between 6-10%; around 30% of the tiles had crazes after the crazing-resistance test; the majority of the tiles had moisture expansion, after boiling, between 0,0% and 0,03%, being indicated in the NBR 13818 norm that expansions above 0,06% may contribute to problems in the tiles service, the boiling seem to cause an kind of erosion in the test samples during the test to determine the moisture expansion; the analyze using phase diagrams indicated that the studied tiles have a decreasing relation between the water absorption and the estimated quantity of glass phase, and a decreasing behavior between the moisture expansion, after boiling, and the estimated quantity of glass phase and that the obtained values of the linear thermal expansion coefficient were situated in the range of 6 to 8 x 10"6 °C"', being indicated in the EN 103 norm, that the these values have to be inferiors to 9 x 10"6 °C"1, when the ceramic tiles are processed by pressing.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1971 |
| Date | 16 October 2018 |
| Creators | MENEZES, Romualdo Rodrigues. |
| Contributors | FERREIRA, Heber Carlos., MELO, Dulce Maria de Araújo., KIMINAMI, Ruth Herta Goldschimidt Aliaga. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICA, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | ATECEL |
Page generated in 0.0033 seconds