This work is concerned with mechanical property improvements to poly(ethylene terephthalate), PET, fibers by the addition of layered silicate nanoparticles and by drawing the un-oriented nanocomposite filaments in a second step. No previous studies on PET fibers filled with montmorillonite (MMT) nanoclay examined fiber drawability at temperatures above the glass transition. Therefore, the primary objective of this research was to determine 1) if PET nanocomposite fibers could be drawn to finer diameters and 2) whether drawing imparted improved Young's modulus and tenacity (i.e. strength) relative to un-filled PET fibers. Of equal importance to this work, the subsequent objective was to discern and understand the role of nanoclay in 1) the production of improved or reduced mechanical properties and 2) the ability to draw PET to lower or higher than normal draw ratios.
In the first part of this thesis, the improvements in Young's modulus and tenacity of PET fibers filled with various types of organically modified montmorillonite is shown and the method to produce them is discussed. Greater improvements in mechanical properties occurred when the MMT stacks were intercalated with PET. A nominal 1 wt% loading of dimethyl-dehydrogenated tallow quaternary ammonium surface modified MMT in drawn PET fiber showed a 28% and 63% increase in Young's modulus and strength, respectively. Relative to an un-filled PET fiber, these results exceeded the upper-bound of the rule of mixtures estimate. Therefore, both the type of surface modification and concentration of MMT were shown to affect the degree of PET orientation and crystallinity. Furthermore, drawability above Tg and elongation-at-break increased upon the addition of organically modified MMT to un-oriented PET fibers, which was a key distinction of this work from others examining similar systems.
Interestingly, the mechanical properties of modulus and tenacity showed a maximum with concentration of alkyl modified clay, but drawability did not show significant variation with increasing nanoclay content. Thermal analysis and Raman spectroscopy was used to examine the role of nanoclay in creating this maximum in mechanical properties. At low loadings, nanoclay was shown to intercalate with PET and enhance amorphous orientation. At higher concentrations of nanoclay the presence of large agglomerates prevented efficient orientation to the fiber axis and acted as stress concentrators to aid in cavitation and failure during testing. Raman spectroscopy showed that the as-spun unfilled PET fibers possessed significantly more trans conformer content of the ethylene glycol moiety than the nanocomposite fibers. The greater gauche content of the nanocomposite fibers delayed crystalline development during non-isothermal DSC scans to higher temperatures was associated with the increased drawability. / Ph. D.
| Identifer | oai:union.ndltd.org:VTETD/oai:vtechworks.lib.vt.edu:10919/27175 |
| Date | 27 May 2008 |
| Creators | Litchfield, David W. |
| Contributors | Chemical Engineering, Baird, Donald G., Walz, John Y., Wilkes, Garth L., Lesko, John J., Davis, Richey M. |
| Publisher | Virginia Tech |
| Source Sets | Virginia Tech Theses and Dissertation |
| Detected Language | English |
| Type | Dissertation |
| Format | application/pdf |
| Rights | In Copyright, http://rightsstatements.org/vocab/InC/1.0/ |
| Relation | Litchfield_Dissertation2.pdf |
Page generated in 0.0021 seconds