Orientadores: Rafael Leonardo Xediek Consani, Janaína de Cássia Orlandi Sardi / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-23T21:37:58Z (GMT). No. of bitstreams: 1
Silva_ManoelaCapladeVasconcellosdosSantosda_D.pdf: 1387678 bytes, checksum: 17ea18ac10fef54c8580345c3bba0454 (MD5)
Previous issue date: 2013 / Resumo: Este trabalho avaliou o efeito do número de ciclos de desinfecção por energia de micro-ondas na dureza Knoop, rugosidade e brilho de resinas termopolimerizadas para prótese total. Foram confeccionados 20 corpos-de-prova de cada material medindo 20 mm de diâmetro por 2 mm de altura, os quais foram distribuídos em 6 grupos de acordo com as resinas: QC-20, Onda Cryl, Clássico, Vipi Cril, Vipi Wave e Vipi Caracterizada. Todos os corpos-de-prova foram submetidos aos ensaios de rugosidade, dureza e brilho antes (controle, dia 0) e em cada ciclo de desinfecção (7, 14, 21 e 28 dias). Os corpos-de-prova foram polimerizados de acordo com as recomendações dos fabricantes, desincluídos e o acabamento realizado com pedra abrasiva para resina, lixas de carbeto de silício e pastas para polimento. A desinfecção por micro-ondas foi realizada a 650 W por 3 minutos, uma vez por dia durante 28 dias. Entre as desinfecções, as amostras permaneceram imersas em água e armazenadas em estufa a 37°C. Nos ensaios de rugosidade e dureza Knoop foram realizadas três mensurações na superfície de cada corpo-de-prova, sendo registrada a média das leituras. Os valores de brilho foram mensurados com medidor de brilho e para cada corpo-de-prova foram realizadas quatro mensurações, uma em cada quadrante, com feixe de luz incidindo em 60 graus. Os valores obtidos foram submetidos à ANOVA dois fatores para medidas repetidas, e teste de Tukey (5%). Os resultados mostraram que a resina Clássico apresentou o maior e a Vipi Wave o menor valor de rugosidade. Quando se avaliou a dureza, a resina Onda Cryl apresentou os maiores valores nos ciclos de 14 e 21 dias e não houve diferença estatística nos valores de dureza Knoop entre as demais resinas. A resina QC-20 apresentou os maiores valores de brilho, sendo maiores no controle (dia 0) e nos ciclos de 7 e 14 dias, os quais foram diferentes estatisticamente dos ciclos de 21 e 28 dias. Concluiu-se que houve influência da desinfecção por micro-ondas na rugosidade e dureza de todas as resinas, independente do número de ciclos. Com exceção da Clássico, as demais resinas mostraram valores de brilho com diferença estatisticamente significativa entre controle e ciclos de desinfecção / Abstract: This study evaluated the effect of repeated disinfection by microwave irradiation on hardness, surface roughness and gloss of denture base acrylic resins. Twenty samples were prepared for each material measuring 20 mm in diameter and 2 mm in height, which were divided into six groups according to the resins: QC-20, Wave Cryl, Classico, Vipi Cril, Vipi Wave and Vipi Characterized. All samples were tested for roughness, hardness and gloss analysis before and after disinfection cycles. Samples were polymerized according to the manufacturers' recommendations, deflasked and finished with abrasive stones, silicon carbide abrasives and polishing slurry. Disinfection by microwave irradiation was made at 650 W for 3 minutes, one time by day during 28 days. Between disinfection cycles the samples were stored in an incubator at 37°C. Three roughness measurements were made on the polished surface and the average was recorded as the roughness value (Ra, mm) for each sample. Hardness was recorded with three Knoop penetrations with a load of 50 kgf for 10 seconds. Three readings of each sample were used to obtain arithmetic mean for each analysis. The gloss values were measured with glossmeter. Four measurements were performed in each sample, one in each quadrant focusing the light beam at 60 degrees. The readings were recorded as the value of unit gloss (Gloss Unit - GU) and the data were recorded in the software. The values obtained were subjected to two-way ANOVA for repeated measures and Tukey's test (5%). The results showed that Classico had the highest value and Vipi Wave the lowest for surface roughness. Onda Cryl showed the highest values for hardness at 14- and 21-day cycles and there was no statistical difference among other resins. For gloss, QC-20 resin showed the highest values being higher at control and 7- and 14-day cycles, statistically different from 21- and 28-day cycles. It was concluded that there was influence of microwave irradiation in the roughness and hardness for all resins, regardless the number of cycles. Whit exception of Classico, there was statistically significant difference in gloss for all acrylic resins / Doutorado / Protese Dental / Mestre em Clínica Odontológica
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288562 |
Date | 23 August 2018 |
Creators | Silva, Manoela Capla de Vasconcellos dos Santos da, 1983- |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Sardi, Janaina de Cassia Orlandi, Consani, Rafael Leonardo Xediek, 1974-, Júnior, Franciso de Assis Mollo, Filho, João Neudenir Arioli, Henriques, Ghuilherme Elias Pessanha, Santos, Mateus Bertolini Fernandes dos |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | 69 f. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.002 seconds