Orientador: Frab Norberto Boscolo / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-04T04:17:51Z (GMT). No. of bitstreams: 1
Terra_EtienneRomanelli_M.pdf: 924097 bytes, checksum: 3d167bca45ac0474585a5d784fe9ec2a (MD5)
Previous issue date: 2005 / Resumo: Como a maioria dos pacientes que se submetem à radioterapia na região de cabeça e pescoço possuem restaurações de compósitos na cavidade bucal, qualquer efeito interativo entre o feixe de radiação ionizante incidente e o material restaurador será clinicamente significativo, se as propriedades do material forem alteradas pela radiação. Desconhecendo-se os efeitos dos raios X, produzidos por um acelerador linear, no compósito odontológico FilteK Z250 (3M), foram realizados estudos para avaliar as possíveis alterações nas propriedades físicas, mecânicas e químicas deste compósito após a irradiação. Foram confeccionados 100 corpos-de-prova e mantidos armazenados durante todo o experimento a 37°C e 100% de umidade relativa do ar. O grupo 0 não irradiado foi composto por vinte corpos-de-prova, enquanto os demais corpos-de-prova foram aleatoriamente divididos em quatro grupos, conforme as doses de radiação X recebidas: 1, 2, 5 e 10Gy. Foram utilizados metade dos corpos-de-prova de cada um dos grupos para a análise de rugosidade de superfície e resistência à abrasão, e os demais, para a análise de dureza Knoop e espectrometria de Infravermelho com Transformações de Fourier. Os dados obtidos foram submetidos à análise de variância para medidas repetidas e teste de Tukey (a = 0,05). No período avaliado, houve um aumento estatisticamente significante na dureza Knoop superficial induzida pela irradiação de 10Gy de raios X, indicando uma polimerização adicional no compósito fotopolimerizado, porém, a resistência à abrasão e a rugosidade superficial do compósito Z250 não foram afetadas pelos raios X, quando o compósito foi irradiado até a dose de 10Gy. Os resultados obtidos por meio dos espectros de infravermelho, mostraram que em todas as doses avaliadas alguns grupos funcionais foram consumidos e novos grupos foram formados quando comparados com a amostra não irradiada. Assim, verificou-se que a irradiação (nas doses de 1, 2, 5 e 10Gy) durante o período avaliado não promoveu efeitos prejudiciais no compósito Z250, apesar das alterações no seu espectro químico / Abstract: Since most patients submitted to radiotherapy of the head and neck have composite restorations, any interactive effect between ionizing radiation and restorative material will be clinically significant if the material properties are altered by radiation. Due to the lack of knowledge on the effects of X rays produced by a linear accelerator on the dental composite Filtek Z250 (3M), this study was undertaken to evaluate the possible alterations in the physical, mechanical and chemical properties of this composite after irradiation. One hundred specimens were fabricated and stored at 37ºC and 100% relative humidity of air throughout the study. Group 0 was not irradiated and comprised twenty specimens, and the other specimens were randomly divided into four groups, according to the X-ray doses received: 1, 2, 5 and 10Gy. Half of the specimens of each group were used for analysis of surface roughness and abrasion resistance, and the others were submitted to the Knoop hardness test and Fourier Transform Infrared Spectrometry. Data were submitted to analysis of variance for repeated measurements and to the Tukey test (a = 0.05). In the study period, there was a statistically significant increase in the surface Knoop hardness induced by irradiation with 10Gy of X rays, indicating additional curing of the light-cured composite, yet the abrasion resistance and surface roughness of the composite Z250 were not affected by the X rays when the composite was irradiated with up to 10Gy. The results obtained by the infrared spectra demonstrated that, for all dosages evaluated, some functional groups are consumed and new groups are formed when compared to the non-irradiated sample. Thus, it was observed that irradiation (doses 1, 2, 5 and 10Gy) during the period evaluated did not yield any harmful effects on the composite Z250, despite the alterations in its chemical spectrum / Mestrado / Radiologia Odontologica / Mestre em Radiologia Odontológica
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288914 |
Date | 21 February 2005 |
Creators | Terra, Etienne Romanelli |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Boscolo, Frab Norberto, 1942-, Castilho, Julio Cezar de Melo, Almeida, Solange Maria de |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | 41 f. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.002 seconds