The aim of the study presented in this thesis is to explore the electrical and physical properties of films of tin and lead clusters. Understanding the novel conductance properties of cluster films and related phenomenon such as coalescence is important to fabricate any cluster based devices.
Coalescence is an important phenomenon in metallic cluster films. Due to coalescence the morphology of the films changes with time which changes their properties and could lead to failure in cluster devices. Coalescence is studied in Sn and Pb cluster films deposited on Si$_3$N$_4$ surfaces using Ultra High Vacuum (UHV) cluster deposition system. The conductance of the overall film is linked to the conductance of the individual necks between clusters by simulations. It is observed that the coalescence process in Sn and Pb films follows a power law in time with an exponent smaller than reported in literature. These results are substantiated by the results from previous experimental and Kinetic Monte Carlo (KMC) simulation studies at UC.
Percolating films of Sn show unique conductance properties. These films are characterized using various electrode configurations, applied voltages and temperatures. The conductance measurements are performed by depositing clusters on prefabricated gold electrodes on top of Si$_3$N$_4$ substrates. Sn cluster films exhibit a variety of conductance behaviours during and after the end of deposition. It is observed that the evolution of conductance during the onsets at percolation threshold is dependent on the film morphology. Samples showing difference responses in onset also behave differently after the end of deposition. Therefore all samples were categorized according to their onset behaviour.
After the end of deposition, when a bias voltage is applied, the conductance of Sn films steps up and down between various well-defined conductance levels. It is also observed that in many cases the conductance levels between which these devices jump are close to integral multiples of the conductance quantum. There are many possible explanations for the steps in conductance. One of the explanations is formation and breaking of conducting paths in the cluster films by electric field induced evaporation and electromigration respectively. The stepping behaviour is similar to that in non-volatile memory devices and hence very interesting to explore due to potential applications.
Identifer | oai:union.ndltd.org:canterbury.ac.nz/oai:ir.canterbury.ac.nz:10092/6677 |
Date | January 2011 |
Creators | Sattar, Abdul |
Publisher | University of Canterbury. Physics and Astronomy |
Source Sets | University of Canterbury |
Language | English |
Detected Language | English |
Type | Electronic thesis or dissertation, Text |
Rights | Copyright Abdul Sattar, http://library.canterbury.ac.nz/thesis/etheses_copyright.shtml |
Relation | NZCU |
Page generated in 0.0014 seconds