In this study it was proposed to investigate the use of 3D metal oxides (specifically titanium oxides) as potential electrode materials for lithium ion batteries. Three different approaches were taken: mesoporous materials to increase the surface area and improve the capacity; nanocrystalline materials to increase the surface area and to investigate any changes that may occur using nanocrystals; and microporous materials that are more open, allowing rapid diffusion of lithium and higher capacities. Of the three categories of materials studies, mesoporous TiO2 was the least promising with low reversible capacities (20 mAh??g-1) due to densification resulting in a loss of surface area. In nanocrystalline rutile an irreversible phase change occurred upon initial intercalation, however after this intercalation occurred reversibly in a single phase mechanism giving capacities of 100 mAh??g-1. A trend in intercalation potential was observed with crystallite size that was related to the ability of the structure to relax and accept lithium. Doping of rutile yielded no real improvement. Brookite gave only low capacities from a single phase intercalation mechanism. TiO2 films produced by a novel electrochemical technique showed that while amorphous films give greater capacities, more crystalline (anatase) films give greater reversibility. Overall, microporous titanosilicates showed the most promise with sitinakite giving a reversible capacity of 80 mAh??g-1 after twenty cycles or double this when dried. The intercalation was found to occur by two steps that generate large changes in crystallite size explaining the capacity fade witnessed. While doping did not improve the performance, cation exchange has proven beneficial. The remaining titanosilicates did not perform as well as sitinakite, however a trend was observed in the intercalation potentials with the wavenumber of the Ti-O Raman stretch. This was due to the covalent nature of the bonding. Upon reduction an electron is added to the bond meaning the energy of the bond determines intercalation potential. Overall, most promise was shown by the microporous titanosilicates. The capacities of sitinakite after drying, are comparable to those of the "zero strain" material Li4Ti5O12. Investigation of the titanosilicates and their ion-exchanged derivatives is a promising path for new lithium-ion battery electrode materials.
| Identifer | oai:union.ndltd.org:ADTP/187651 |
| Date | January 2007 |
| Creators | Milne, Nicholas A, Chemical Sciences & Engineering, Faculty of Engineering, UNSW |
| Source Sets | Australiasian Digital Theses Program |
| Language | English |
| Detected Language | English |
| Rights | http://unsworks.unsw.edu.au/copyright, http://unsworks.unsw.edu.au/copyright |
Page generated in 0.0009 seconds